Experimental determination and thermodynamic reassessment of the Al-Cr-Ru ternary system

被引：0
作者：
Ma, Du-pei [1 ]
Ke, Sheng-kun [1 ]
Li, Zhi [1 ,2 ]
Hu, Jing-xian [1 ,2 ]
Yin, Fu-cheng [1 ,2 ]
Liu, Yan [1 ,2 ]
Liu, Ye [1 ,2 ]
机构：
[1] Xiangtan Univ, Sch Mat Sci & Engn, Xiangtan 411105, Peoples R China
[2] Xiangtan Univ, Key Lab Mat Design & Preparat Technol Hunan Prov, Xiangtan 411105, Peoples R China
来源：
INTERMETALLICS | 2024年 / 173卷
基金：
中国国家自然科学基金;
关键词：
Al; Cr-Ru ternary system; Phase equilibria; CALPHAD; Thermodynamic assessment; PHASE-DIAGRAM; RICH PART; TEMPERATURE; RUTHENIUM; MICROSTRUCTURE; EQUILIBRIA; STABILITY; CHROMIUM; ALLOYS;
D O I：
10.1016/j.intermet.2024.108404
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
The isothermal sections at 950 degrees C and 1150 degrees C of Al-Cr-Ru ternary system were determined experimentally by equilibrium alloy method, combined with X-ray diffraction, scanning electron microscopy and energy-dispersive spectrometric. Nine and eight three-phase equilibria were confirmed at the 950 degrees C and 1150 degrees C isothermal sections of the Al-Cr-Ru ternary systems, respectively. The liquids surface projection of the Al-Cr-Ru ternary system was determined by identifying the microstructures of the as-cast alloys, and seven primary solidification regions were determined in the liquids surface projection. Besides, the ternary compound tau 2 was identified as end-centered monoclinic structure by transmission electron diffraction analysis. The lattice parameters of the tau 2 phase are a = 0.5175 nm, b = 1.7532 nm, c = 0.5150 nm and alpha = gamma = 90 degrees, beta = 79.167 degrees. Based on the available data of the Al-Cr-Ru ternary system and related binary systems, thermodynamic reassessment of the Al-Cr-Ru ternary system was performed using the Calculation of Phase Diagram approach. A new thermodynamic database for the Al-Cr-Ru ternary system was obtained, and the experimental data are consistent well with the calculated results.
引用
收藏
页数：17
相关论文
共 55 条
  • [31] The Al-Cr (aluminum-chromium) system
    Murray, JZ
    [J]. JOURNAL OF PHASE EQUILIBRIA, 1998, 19 (04): : 368 - 375
  • [32] Obrowski W., 1963, METALL BERLIN, V17, P108
  • [33] Thermodynamic assessment of the Al-Ru system
    Prins, SN
    Cornish, LA
    Stumpf, WE
    Sundman, B
    [J]. CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2003, 27 (01): : 79 - 90
  • [34] Raub E., 1955, J. Zeitschrift fur Metallkunde, V46, P210
  • [35] ALGEBRAIC REPRESENTATION OF THERMODYNAMIC PROPERTIES AND THE CLASSIFICATION OF SOLUTIONS
    REDLICH, O
    KISTER, AT
    [J]. INDUSTRIAL AND ENGINEERING CHEMISTRY, 1948, 40 (02): : 345 - 348
  • [36] The effects of ruthenium on the phase stability of fourth generation Ni-base single crystal superalloys
    Sato, A
    Harada, H
    Yokokawa, T
    Murakumo, T
    Koizumi, Y
    Kobayashi, T
    Imai, H
    [J]. SCRIPTA MATERIALIA, 2006, 54 (09) : 1679 - 1684
  • [37] SAUNDERS N, 1986, MATER SCI TECH SER, V2, P521, DOI 10.1179/026708386790329055
  • [38] DIE VERBINGUNGEN RUAL2 UND OSSI1,5
    SCHWOMMA, O
    WITTMANN, A
    NOWOTNY, H
    [J]. MONATSHEFTE FUR CHEMIE, 1963, 94 (05): : 924 - &
  • [39] Shurin A.K., 1964, J. Sb. Nauchn. Rub. Inst. Metallofiz. Akad. Nauk Ukr. SSR, V18, P170
  • [40] Development of a database for the prediction of phases in Pt-Al-Cr-Ru alloys for high-temperature and corrosive environments: Al-Cr-Ru
    Suess, R.
    Watson, A.
    Cornish, L. A.
    Compton, D. N.
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 476 (1-2) : 176 - 186
123456