Different effects of TiB2 particles on corrosion behaviors of in-situ TiB2/ 7075 composites in active and passive environments

被引：7

作者：

Li, Keneng ^{[1
]}

Wang, Zhiping ^{[2
]}

Wang, Fangming ^{[3
]}

Geng, Jiwei ^{[1
]}

Li, Yugang ^{[1
,4
]}

Xia, Peikang ^{[1
,4
]}

Chen, Dong ^{[1
,4
]}

Wang, Haowei ^{[1
,4
]}

机构：

[1] Shanghai Jiao Tong Univ, State Key Lab Met Matrix Composites, Shanghai 200240, Peoples R China

[2] Nanjing Univ Sci & Technol, Herbert Gleiter Inst Nanosci, Sch Mat Sci & Engn, Nanjing 210094, Peoples R China

[3] CNPC Engn Technol R&D Co Ltd, Beijing 102206, Peoples R China

[4] Huaibei Normal Univ, Anhui Prov Ind Gener Technol Res Ctr Alum Mat, Huaibei 235000, Anhui, Peoples R China

来源：

CORROSION SCIENCE | 2024年 / 235卷

基金：

中国国家自然科学基金;

关键词：

Intergranular corrosion; Exfoliation corrosion; Metal matrix composites; In-situ observation; ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY; EXFOLIATION CORROSION; MECHANICAL-PROPERTIES; ALUMINUM-ALLOYS; HEAT-TREATMENT; AL; MICROSTRUCTURE; STRENGTH; CRACKING; PRECIPITATION;

D O I：

10.1016/j.corsci.2024.112201

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The different effects of TiB2 on intergranular corrosion (IGC) and exfoliation corrosion (EXCO) in TiB2/7075 composites were investigated. Lower particle content accelerated IGC due to the first dissolution of large TiB2/Al interface precipitates, causing TiB2 deposition in corrosion channels. Conversely, higher particle content reduced the maximum IGC depth to 47 % with dense corrosion products inhibiting penetration of corrosive solution. EXCO weight loss increased by 271 % and 388 % with 3.5 wt% and 7 wt% particles, respectively. Micro-galvanic corrosion and recrystallization caused by particles reduced EXCO resistance. The passive IGC environment and active EXCO environment lead to different corrosion resistances of composites.

引用

页数：18

共 74 条

[71] Consideration of Orowan strengthening effect in particulate-reinforced metal matrix nanocomposites: A model for predicting their yield strength [J].

Zhang, Z ;

Chen, DL .

SCRIPTA MATERIALIA, 2006, 54 (07) :1321-1326

[72] Interface precipitation and corrosion mechanisms in a model Al-Zn-Mg-Cu alloy strengthened by TiC particles [J].

Zhao, Kai ;

Han, Guang ;

Gao, Tong ;

Yang, Huabing ;

Qian, Zhao ;

Hu, Kaiqi ;

Liu, Guiliang ;

Nie, Jinfeng ;

Liu, Xiangfa .

CORROSION SCIENCE, 2022, 206

[73] Corrosion and passive behavior of AlxCrFeNi3-x (x=0.6, 0.8, 1.0) eutectic high entropy alloys in chloride environment [J].

Zhao, Qiancheng ;

Pan, Zhimin ;

Wang, Xuefei ;

Luo, Hong ;

Liu, Yang ;

Li, Xiaogang .

CORROSION SCIENCE, 2022, 208

[74] Grain boundary segregation of alloying Cu induced intergranular corrosion of B4C-6061Al composite [J].

Zhou, Y. T. ;

Zan, Y. N. ;

Wang, Q. Z. ;

Xiao, B. L. ;

Ma, Z. Y. ;

Ma, X. L. .

MATERIALS CHARACTERIZATION, 2021, 173

← 1 2 3 4 5 6 7 8 →