Intrinsically Microporous Polyimides Derived from 2,2′-Dibromo-4,4′,5,5′-bipohenyltetracarboxylic Dianhydride for Gas Separation Membranes

This work aims to expand the structure-property relationships of bromo-containing polyimides and the influence of bromine atoms on the gas separation properties of such materials. A series of intrinsically microporous polyimides were synthesized from 2,2 '-dibromo-4,4 ',5,5 '-bipohenyltetracarboxylic dianhydride (Br-BPDA) and five bulky diamines, (7,7 '-(mesitylmethylene)bis(8-methyldibenzo[b,e][1,4]dioxin-2-amine) (MMBMA), 7,7 '-(Mesitylmethylene)bis(1,8-dimethyldibenzo[b,e][1,4] dioxin-2-amine) (MMBDA), 4,10-dimethyl-6H,12H-5,11-methanodibenzo[b,f][1,5]diazocine-2,8-diamine (TBDA1), 4,10-dimethyl-6H,12H-5,11-methanodibenzo[b,f][1,5]diazocine-3,9-diamine (TBDA2), and (9R,10R)-9,10-dihydro-9,10-[1,2]benzenoanthracene-2,6-diamine (DAT). The Br-BPDA-derived polyimides exhibited excellent solubility, high thermal stability, and good mechanical properties, with their tensile strength and modulus being 59.2-109.3 MPa and 1.8-2.2 GPa, respectively. The fractional free volumes (FFVs) and surface areas (SBET) of the Br-BPDA-derived polyimides were in the range of 0.169-0.216 and 211-342 m(2) g(-1), following the order of MMBDA > MMBMA > TBDA2 > DAT > TBDA1, wherein the Br-BPDA-MMBDA exhibited the highest SBET and FFV and thus highest CO2 permeability of 724.5 Barrer. Moreover, Br-BPDA-DAT displayed the best gas separation performance, with CO2, H-2, O-2, N-2, and CH4 permeabilities of 349.8, 384.4, 69.8, 16.3, and 19.7 Barrer, and H-2/N-2 selectivity of 21.4. This can be ascribed to the ultra-micropores (<0.7 nm) caused by the high rigidity of Br-BPDA-DAT. In addition, all the bromo-containing polymers of intrinsic microporosity membranes exhibited excellent resistance to physical ageing.