Experimental Study on the Process of Submerged Arc Welding for Nickel-Based WC Flux-Cored Wire on Descaling Roll

被引:1
作者
Li, Chang [1 ]
Feng, Lei [1 ]
Han, Xing [1 ]
Luo, Fenghua [2 ]
Sun, Han [1 ]
机构
[1] Univ Sci & Technol Liaoning, Coll Mech Engn & Automat, Anshan 114051, Peoples R China
[2] Cent South Univ, State Key Lab Powder Met, Changsha 410083, Peoples R China
关键词
descaling rolls; flux-cored wire; submerged arc welding; nickel-based WC; surfacing layer structure; post-welding evaluation; MICROSTRUCTURE; TEMPERATURE; STEEL;
D O I
10.3390/coatings14060734
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Descaling roll is a key component used to remove iron oxide on billet surface in hot rolling production lines, and its surface properties have a significant effect on the quality of hot rolling products. The descaling roll is in bad service condition and subjected to the dynamic impact caused by high-pressure water erosion and high temperature billet descaling process for a long time. Under the action of high temperature, strong wear, multi-cycle heat, force, flow and multi-field strong coupling, the surface is prone to wear and corrosion failure, which affects the continuous rolling production. Submerged arc welding provides an effective way to repair and strengthen the descaling roll surface. The content of WC hard phase has a significant effect on welding quality. At the same time, direct submerged arc welding of Ni based WC wire on the descaling roll surface is easy to cause cracks, and a gradient synergistic strengthening effect can be formed by setting the transition bottom layer in welding. At present, there is a lack of experiments related to the preparation of flux-cored wire with different contents and the overlaying for the bottom submerged arc welding. Relevant studies are urgently needed to further reveal the welding process mechanism to provide significant theoretical support for the preparation of wire materials and the improvement of welding quality. In this paper, 30% and 60% WC flux-cored wires were prepared by employing Ni-Cr-B-Si alloy powder as the base powder, and submerged arc welding tests were conducted on the descaling roll, preparing three welding layers, namely 70% NiCrBSi + 30% WC without the bottom layer, 70% NiCrBSi + 30% WC with the bottom layer, and 40% NiCrBSi + 60% WC with the bottom layer. The properties of the welding layer were evaluated by SEM, XRD, EDS, hardness, friction and wear, corrosion and impact experiments. The results show that the WC hard phase added in the filler metal has dissolved and formed a new phase with other elements in the melting pool. The surfacing layer mainly contains Fe-Ni, Cr-C, Fe3Si, Ni3C and other phases. The surfacing layer prepared by a different amount of WC flux-cored wire and the surfacing layer with or without the bottom layer have great differences in microstructure and properties. This study lays a significant theoretical foundation for optimizing the submerged arc welding process and preparing welding materials for the descaling roll and has significant practical significance and application value.
引用
收藏
页数:22
相关论文
共 29 条
  • [1] [Anonymous], 2020, GB/T229-2020
  • [2] Comparative Investigation of Multi-stranded Wire and Single Wire in Submerged Arc Welded Joints of Duplex Stainless Steel: Microstructure and Pitting Properties
    Chen, Zefang
    Peng, Kang
    Chen, Xizhang
    Wang, Qichen
    Liang, Yu
    [J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (10) : 4976 - 4986
  • [3] Closure behavior of spherical void in slab during hot rolling process
    Cheng, Rong
    Zhang, Jiongming
    Wang, Bo
    [J]. METALLURGICAL RESEARCH & TECHNOLOGY, 2018, 115 (03)
  • [4] Influence of Modifying Nanoadditives on the Properties of a Multilayer Composite Coating Obtained by Laser Surfacing
    Cherepanov, A. N.
    Orishich, A. M.
    Ovcharenko, V. E.
    Malikov, A. G.
    Drozdov, V. O.
    Pshenichnikov, A. P.
    [J]. PHYSICS OF METALS AND METALLOGRAPHY, 2019, 120 (01) : 101 - 106
  • [5] Chmielewski Tomasz, 2015, Welding International, V29, P861, DOI 10.1080/09507116.2014.937604
  • [6] Mathematical modeling and intelligent optimization of submerged arc welding process parameters using hybrid PSO-GA evolutionary algorithms
    Choudhary, Ankush
    Kumar, Manoj
    Gupta, Munish Kumar
    Unune, Deepak Kumar
    Mia, Mozammel
    [J]. NEURAL COMPUTING & APPLICATIONS, 2020, 32 (10) : 5761 - 5774
  • [7] Experimental investigation and optimization of weld bead characteristics during submerged arc welding of AISI 1023 steel
    Choudhary, Ankush
    Kumar, Manoj
    Unune, Deepak Rajendra
    [J]. DEFENCE TECHNOLOGY, 2019, 15 (01) : 72 - 82
  • [8] Investigations of Cavitation Erosion and Corrosion Behavior of Flame-Sprayed NiCrBSi/WC-12Co Composite Coatings
    Ciubotariu, Costel-Relu
    Frunzaverde, Doina
    Marginean, Gabriela
    [J]. MATERIALS, 2022, 15 (08)
  • [9] Effective role of short time furnace heat treatment and laser treatment on the residual stress and mechanical properties of NiCrBSi-WC weldments produced using plasma transferred arc welding process
    Deenadayalan, K.
    Murali, Vela
    Elayaperumal, A.
    Arulvel, S.
    [J]. JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2021, 15 : 3492 - 3513
  • [10] Role of various weight percentages of WC particle on interface thickness and friction-wear property of NiCrBSi-WC composite fabricated using PTAW process
    Deenadayalan, K.
    Murali, Vela
    [J]. MATERIALS RESEARCH EXPRESS, 2019, 6 (04)