Influence of cathodic polarization on stress corrosion cracking susceptibility of 35CrMo steel for high strength bolt in simulated deep-sea environment

被引：3
作者：
Zhao, Rongrong [1 ,2 ]
Xu, Likun [1 ,2 ]
Xin, Yonglei [1 ,2 ]
Xuan, Junji [3 ]
Bai, Shuangfeng [2 ]
Xue, Lili [1 ]
Li, Li [1 ]
Teng, Yizheng [2 ]
Guo, Mingshuai [1 ,2 ]
Hou, Jian [2 ]
Guo, Weimin [2 ]
Li, Bingzhi [2 ]
机构：
[1] Harbin Engn Univ, Coll Mat Sci & Chem Engn, Harbin 150001, Peoples R China
[2] Luoyang Ship Mat Res Inst, Natl Key Lab Marine Corros & Protect, Qingdao 266237, Peoples R China
[3] Luoyang Ship Mat Res Inst, Luoyang 471023, Peoples R China
来源：
CORROSION SCIENCE | 2024年 / 233卷
关键词：
Low alloy steel (A); EIS (B); Cathodic protection (C); Hydrogen embrittlement (C); Stress corrosion (C); X70 PIPELINE STEEL; HYDROGEN EMBRITTLEMENT; HYDROSTATIC-PRESSURE; CALCAREOUS DEPOSITS; STAINLESS-STEEL; FRACTURE-BEHAVIOR; DELAYED FRACTURE; GRAIN-BOUNDARY; A514; STEEL; X65;
D O I：
10.1016/j.corsci.2024.112079
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of cathodic polarization on stress corrosion cracking (SCC) of 35CrMo steel for high strength bolt in the simulated deep-sea environment has been studied. The results show that 35CrMo steel has a higher SCC sensitivity at open circuit potential in the simulated deep-sea environment than that in the shallow seawater. With potential negatively shifted to -750 mV, 35CrMo steel presents the lowest SCC sensitivity. And the SCC susceptibility is increased significantly with the further negative shift of potential because of the intensive hydrogen evolution. When the potential is below -950 mV, hydrogen embrittlement with hydrogen-enhanced-plasticity mediated decohesion should be the dominant SCC micro-mechanism.
引用
收藏
页数：17
相关论文
共 32 条
  • [21] Effect of the calcareous deposits on the cathodic protection potential of 10Ni5CrMoV high-strength steel in a deep-sea environment by using the response surface methodology
    Xu, Hongbo
    Li, Lin
    Zhao, Yang
    San, Hongyu
    Zhang, Tao
    Su, Xiandong
    Wang, Fuhui
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2021, 72 (04): : 720 - 731
  • [22] Regularities of Stress-Corrosion Cracking of Pipe Steel 09G2S at Cathodic Polarization in a Model Soil Environment
    Nyrkova, L., I
    Lisovyi, P. E.
    Goncharenko, L., V
    Osadchuk, S. O.
    Kostin, V. A.
    Klymenko, A., V
    PHYSICS AND CHEMISTRY OF SOLID STATE, 2021, 22 (04): : 828 - 836
  • [23] Using a pulsed electric current to reduce the susceptibility of high-strength steel to the stress corrosion cracking caused by hydrogen
    Ma, Rui
    Xiang, Siqi
    Zhang, Hexiong
    Zhang, Xinfang
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2020, 45 (15) : 9128 - 9136
  • [24] The effect of hydrogen on stress corrosion behavior of X65 steel welded joint in simulated deep sea environment
    Wan, Hongxia
    Du, Cuiwei
    Liu, Zhiyong
    Song, Dongdong
    Li, Xiaogang
    OCEAN ENGINEERING, 2016, 114 : 216 - 223
  • [25] Effect of sulfate-reducing bacteria and cathodic potential on stress corrosion cracking of X70 steel in sea-mud simulated solution
    Sun, Dongxu
    Wu, Ming
    Xie, Fei
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2018, 721 : 135 - 144
  • [26] Influence of Sulfate-Reducing Bacteria on the Corrosion Behavior of High Strength Steel EQ70 under Cathodic Polarization
    Guan, Fang
    Zhai, Xiaofan
    Duan, Jizhou
    Zhang, Meixia
    Hou, Baorong
    PLOS ONE, 2016, 11 (09):
  • [27] Corrosion fatigue cracking behaviors of Q690qE high-strength bridge steel as a weld joint in simulated marine environment
    Lu, Cuiping
    Yao, Qiong
    Li, Ningning
    Sun, Liyang
    Dai, Wenhe
    Zhang, Chuang
    Ma, Hongchi
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2024, 47 (11) : 4341 - 4355
  • [28] Effect of AC Current Density on the Stress Corrosion Cracking Behavior and Mechanism of E690 High-Strength Steel in Simulated Seawater
    Pan, Yue
    Liu, Zhiyong
    Zhang, Yadan
    Li, Xiaogang
    Du, Cuiwei
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (11) : 6931 - 6941
  • [29] Influence of Ultrasonic Nanocrystal Surface Modification on the Corrosion and Stress Corrosion Cracking Behavior of Low Carbon Steel (ASTM A139) Welded Joint in the Simulated District Heating Environment
    Kim, Yong-Sang
    Kim, Woo-Cheol
    Kim, Jung-Gu
    CORROSION, 2018, 74 (01) : 112 - 122
  • [30] Electrochemical characteristic and stress corrosion behavior of API X70 high-strength pipeline steel under a simulated disbonded coating in an artificial seawater environment
    Wu, Wei
    Liu, Zhiyong
    Li, Xiaogang
    Du, Cuiwei
    JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2019, 845 : 92 - 105
1234