Structural characterization of glutaraldehyde crosslinked starch-based nanofibrous film and adsorption improvement for oyster peptide flavor

The inferior hydrophobicity and mechanical properties of starch-based nanofibrous films significantly restrict their practical application. In view of this, this study prepared octenylsuccinylated starch-pullulan nanofibrous films using electrospinning and glutaraldehyde (GTA) gas-phase crosslinking. After GTA crosslinking, the starchbased nanofibrous films remained white, randomly oriented, smooth, and droplet-free. As the crosslinking time increased from 0 h to 24 h, the mean fibrous diameter augmented from 157.34 nm to 238.66 nm, and the water contact angle rose from 24.30 degrees to 52.49 degrees. Meanwhile, their tensile strength and thermal stability grew, and the mean pore area and elongation at break abated with changes in function groups. The crosslinked starch-based nanofibrous films exhibited an enhanced adsorption capacity for alcohols, ethers, esters, hydrocarbons, and Ncompounds of oyster peptides. Correlation analysis shows that the adsorption capacity of the starch-based nanofibrous films was positively correlated with mean fibrous diameter and water contact angle and negatively correlated with mean pore area. These results provide a theoretical basis for the practical application of crosslinked starch-based nanofibrous film materials in deodorization.