Boosting piezoelectric response and electric-field induced strain in PMN-PT relaxor ferroelectrics

High-performance piezoelectric materials are essential for diverse electromechanical devices, from actuators to sensors and transducers. Here, we synthesized Ce2O3-doped Pb(Mg1/3Nb2/3)O3-0.29PbTiO3 (xCe-PMNT29) solid solutions via conventional solid-state methods. In the x = 2.5 % modified composition, we achieved a notable electrostrain-hysteresis trade-off, enhancing electrostrain (0.2 %), equivalent piezoelectric coefficient d & lowast;33 (1701 pm V-1 at 3 kV cm-1), and reducing strain hysteresis to 8.1 %. Additionally, direct high-temperature piezoelectric characterizations revealed real-time variations in piezoelectric coefficient (d33) and the actual depolarization temperature, with d33 reaching 859 pC N-1 at 53 degrees C and planar electromechanical coupling coefficient (kp) exceeding 70 % within 30-85 degrees C. Leveraging x-ray diffraction (XRD) and piezoelectric force microscopy (PFM), we elucidated synergistic effects between complex nanodomains and local structural heterogeneity, enhancing piezoelectric activity. This study presents a promising approach for improving electromechanical performance and electrostrain in ferroelectrics, with significant potential for practical piezoelectric applications.