Cellulose-based aerogel derived N, B-co-doped porous biochar for high-performance CO2 capture and supercapacitor

The remarkable characteristics of porous biochar have generated significant interest in various fields, such as CO2 capture and supercapacitors. The modification of aerogel-derived porous biochar through activation and heteroatomic doping can effectively enhance CO2 adsorption and improve supercapacitor performance. In this study, a novel N, B-co-doped porous biochar (NBCPB) was synthesized by carbonating and activating the N, B dual-doped cellulose aerogel. N and B atoms were doped in-situ using a modified alkali-urea method. The potassium citrate was served as both an activator and a salt template to facilitate the formation of a well-developed nanostructure. The optimized NBCPB-650-1 (where 650 corresponded to activation temperature and 1 represented mass ratio of potassium citrate activator to carbonized NBCPB-400 precursor) displayed the largest micropore volume of 0.40 cm(3)<middle dot>g(-1) and a high specific surface area of 891 m(2)<middle dot>g(-1), which contributed to an excellent CO2 adsorption capacity of 4.19 mmol<middle dot>g(-1) at 100 kPa and 25 degrees C, a high CO2/N-2 selectivity, and exceptional reusability (retained >97.5 % after 10 adsorption-desorption cycles). Additionally, the NBCPB-650-1 electrode also delivered a high capacitance of 220.9 F<middle dot>g(-1) at 1 A<middle dot>g(-1). Notably, the symmetrical NBCPB-650-1 supercapacitor exhibited a high energy density of 9 Wh<middle dot>kg(-1) at the power density of 100 W<middle dot>kg(-1). This study not only presents the potential application of NBCPB-650-1 material in CO2 capture and electrochemical energy storage, but also offers a new insight into easy-to-scale production of heteroatomic-modified porous biochar.