Effects of dissolved hydrogen on corrosion fatigue crack growth behavior of 316LN stainless steel in high temperature pressurized water environment

被引：10
作者：
Zhao, Y. G. [1 ]
Lu, Y. H. [1 ]
Zhang, X. F. [1 ]
Li, Z. H. [1 ]
Liu, T. G. [1 ]
Shoji, T. [1 ]
机构：
[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China
来源：
CORROSION SCIENCE | 2024年 / 232卷
关键词：
316LN stainless steel; Corrosion fatigue crack growth; Dissolved hydrogen; Threshold stress intensity range; Slip-dissolution; Mechanical fatigue; STRAIN; INITIATION; STRESS; LIFE; WELD;
D O I：
10.1016/j.corsci.2024.112041
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of dissolved hydrogen (DH) on the corrosion fatigue crack growth (CFCG) behavior of 316LN stainless steel (SS) was investigated in high temperature pressurized water. The results indicated that DH slightly increased the CFCG threshold stress intensity range ( Delta K th ) value by 9 % and significantly increased the corrosion fatigue crack growth rate (CFCGR) value by 35 %. On the one hand, DH promoted a large plastic zone formed ahead of the crack tip. On the other hand, DH addition transformed the crack growth mechanism from mainly the slip -dissolution without DH addition to the competition between the slip -dissolution and mechanical fatigue.
引用
收藏
页数：11
相关论文
共 46 条
[1]   Role of hydrogen on the incipient crack tip deformation behavior in α-Fe: An atomistic perspective [J].
Adlakha, I. ;
Solanki, K. N. .
JOURNAL OF APPLIED PHYSICS, 2018, 123 (01)
[2]  
[Anonymous], 2015, Standard test methods for notched bar impact testing of metallic materials, ASTM E23 - 12c
[3]   Fatigue crack initiation and growth in a CrMo steel under hydrogen pressure [J].
Briottet, L. ;
Moro, I. ;
Escot, M. ;
Furtado, J. ;
Bortot, P. ;
Tamponi, G. M. ;
Solin, J. ;
Odemer, G. ;
Blanc, C. ;
Andrieu, E. .
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2015, 40 (47) :17021-17030
[4]   Influences of stress intensity factor and dissolved hydrogen on the fatigue crack growth behavior of low-alloy steel in boiling water reactors [J].
Chen, YY ;
Wang, LH ;
Oung, JC ;
Shih, HC .
CORROSION, 2005, 61 (03) :273-284
[5]   Low cycle fatigue behaviors of type 316LN austenitic stainless steel in 310 °C deaerated water-fatigue life and dislocation structure development [J].
Cho, Hyunchul ;
Kim, Byoung Koo ;
Kim, In Sup ;
Jang, Changheui .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 476 (1-2) :248-256
[6]  
Cho P., 2010, The effects of dissolved hydrogen contents on the low cycle fatigue behaviors of a 316LN stainless steel in simulated PWR conditions, P2010
[7]   Environmentally assisted crack growth in 308L stainless steel weld metal in simulated primary water [J].
Dong, Lijin ;
Han, En-Hou ;
Peng, Qunjia ;
Ke, Wei ;
Wang, Lei .
CORROSION SCIENCE, 2017, 117 :1-10
[8]   Application of atomic simulation for studying hydrogen embrittlement phenomena and mechanism in iron-based alloys [J].
Dong, Linshuo ;
Wang, Shuize ;
Wu, Guilin ;
Gao, Junheng ;
Zhou, Xiaoye ;
Wu, Hong-Hui ;
Mao, Xinping .
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2022, 47 (46) :20288-20309
[9]   Environmentally assisted cracking of forged 316LN stainless steel and its weld in high temperature water [J].
Du, Donghai ;
Wang, Jiamei ;
Chen, Kai ;
Zhang, Lefu ;
Andresen, Peter L. .
CORROSION SCIENCE, 2019, 147 :69-80
[10]   Role of welding residual strain and ductility dip cracking on corrosion fatigue behavior of Alloy 52/52M dissimilar metal weld in borated and lithiated high-temperature water [J].
Gao, Jun ;
Tan, Jibo ;
Jiao, Ming ;
Wu, Xinqiang ;
Tang, Lichen ;
Huang, Yifeng .
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2020, 42 :163-174
12345