The preparation and magnetic properties of FeSiCr/MoS2 soft magnetic composites

被引：3

作者：

Li, Nuolin ^{[1
]}

Feng, Shuangjiu ^{[1
]}

Kan, Xucai ^{[1
]}

Liu, Xiansong ^{[1
]}

Zhang, Cong ^{[1
]}

Zhu, Yong ^{[1
]}

Chi, Shangpeng ^{[1
]}

Sun, Wei ^{[2
]}

机构：

[1] Anhui Univ, Engn Technol Res Ctr Magnet Mat Anhui Prov, Sch Mat Sci & Engn, Anhui Key Lab Magnet Funct Mat & Devices, Hefei 230601, Peoples R China

[2] BGRIMM Technol Grp Co LTD, Beijing 100160, Peoples R China

来源：

PHYSICA SCRIPTA | 2024年 / 99卷 / 06期

基金：

国家重点研发计划;

关键词：

soft magnetic composites; magnetic loss; magnetic permeability; high resistance; LOW CORE LOSS; POWDER CORES; FE; PERMEABILITY;

D O I：

10.1088/1402-4896/ad4e16

中图分类号：

O4 [物理学];

学科分类号：

0702 ;

摘要：

Two-dimensional layered material MoS2 was used as a high-resistance insulating material and coated on FeSiCr magnetic powder, and FeSiCr/MoS2 composites with low loss and high permeability were successfully prepared. The morphology and magnetic properties of FeSiCr/MoS2 composites were analyzed by XRD, SEM and B-H analyzer. The results show that although the addition of MoS2 will dilute the magnetic properties of FeSiCr, it still has high permeability and obviously reduces the magnetic loss of FeSiCr powder. At the same time, the addition of MoS2 also improves the frequency stability and quality factor of the composite powder cores. Especially, when the MoS2 content is 1.5 wt%, FeSiCr/MoS2 composites show the best magnetic properties after annealing at 500 degrees C. with a loss of 330 mW cm(-3) and permeability of 66.75 (B-m = 20 mT and f = 1000 kHz). It can be seen that the MoS2 coating has a good effect on reducing the magnetic loss of powder core, which significantly improves the possibility of application of SMCs at high frequency.