A multi-scale experimental investigation on fatigue crack propagation rate behavior of powder bed fusion-laser beam 316L stainless steel subjected to various heat treatments

被引:4
|
作者
Zhu, Wen [1 ]
Moumni, Ziad [1 ,2 ]
Zhu, Jihong [1 ,3 ]
Zhang, Yahui [1 ]
You, Yajun [4 ]
Zhang, Weihong [1 ]
机构
[1] Northwestern Polytech Univ, State IJR Ctr Aerosp Design & Addit Mfg, Xian 710072, Peoples R China
[2] Inst Polytech Paris, LMI UME, ENSTA Paris, F-91120 Palaiseau, France
[3] Northwestern Polytech Univ, MIIT Lab Met Addit Mfg & Innovat Design, Xian 710072, Peoples R China
[4] North Univ China, Sch Aerosp Engn, Taiyuan 030051, Peoples R China
基金
中国国家自然科学基金;
关键词
Powder bed fusion-laser beam 316L stainless steel; Heat treatment; Microstructural evolutions; Fatigue crack propagation rate behavior; Fatigue life; MECHANICAL-PROPERTIES; ACOUSTIC-EMISSION; GROWTH-BEHAVIOR; MICROSTRUCTURE; STRESS; AUSTENITE; FUTURE;
D O I
10.1016/j.engfracmech.2024.110064
中图分类号
O3 [力学];
学科分类号
08 ; 0801 ;
摘要
In this study, three heat treatments referred to as heat treatment 1 (HT1), HT2, and HT3 were applied to tune the microstructure of powder bed fusion -laser beam (PBF-LB) 316L stainless steel. Furthermore, the fatigue crack propagation rate (FCPR) of as -built PBF-LB 316L specimens and specimens subjected to the three aforementioned heat treatments was thoroughly investigated. To this end, the FCPR was evaluated by a fatigue testing machine combined with an infrared thermal camera, and the Paris law was established to quantitatively assess the FCPR of PBF-LB 316L. In addition, a systematic investigation of microstructural evolution, residual stress, tensile properties, and fatigue crack propagation (FCP) fracture surfaces as well as their effect on the FCPR in function of various heat treatments were carried out. The results indicate that the release of residual stresses, the annihilation of the cellular structure, and the occurrence of recrystallization are obtained through the application of HT1, HT2, and HT3 respectively. Furthermore, it is shown that although all three heat treatments can improve the FCPR behavior of PBF-LB 316L to some extent, HT3 PBF-LB 316L presents the lowest FCPR mainly due to its most pronounced plasticityinduced crack closure effect, indicating its highest resistance to FCP even though the recrystallization obtained by HT3 results in the lowest yield strength (YS). Finally, some recommendations about adequate heat treatments concerning fatigue life are suggested.
引用
收藏
页数:23
相关论文
共 50 条
  • [31] Laser Powder Bed Fusion of 316L Stainless Steel: Effect of Laser Polishing on the Surface Morphology and Corrosion Behavior
    Liu, Jun
    Ma, Haojun
    Meng, Lingjian
    Yang, Huan
    Yang, Can
    Ruan, Shuangchen
    Ouyang, Deqin
    Mei, Shuwen
    Deng, Leimin
    Chen, Jie
    Cao, Yu
    MICROMACHINES, 2023, 14 (04)
  • [32] Investigation on the characteristics of porosity, melt pool in 316L stainless steel manufactured by laser powder bed fusion
    Liu, Cheng-song
    Xue, Xiao
    Wang, Yong
    Zhang, Hua
    Li, Jie
    Lu, Yuan-yuan
    Xiong, Li
    Ni, Hong-wei
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 32 : 1832 - 1844
  • [33] Understanding Melt Pool Behavior of 316L Stainless Steel in Laser Powder Bed Fusion Additive Manufacturing
    Zhang, Zilong
    Zhang, Tianyu
    Sun, Can
    Karna, Sivaji
    Yuan, Lang
    MICROMACHINES, 2024, 15 (02)
  • [34] Correlation between microstructure and cyclic behavior of 316L stainless steel obtained by Laser Powder Bed Fusion
    Liang, Xiaoyu
    Hor, Anis
    Robert, Camille
    Salem, Mehdi
    Morel, Franck
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2022, 45 (05) : 1505 - 1520
  • [35] Electrochemical behavior of laser powder bed fusion fabricated 316L stainless steel in a nitric acid solution
    Soleimani, Sahar
    Yeganeh, Mahdi
    Lari Baghal, Seyed Mohammad
    JOURNAL OF LASER APPLICATIONS, 2022, 34 (04)
  • [36] Effects of crystallographic orientation on the corrosion behavior of stainless steel 316L manufactured by laser powder bed fusion
    Trisnanto, Satria Robi
    Wang, Xianglong
    Brochu, Mathieu
    Omanovic, Sasha
    CORROSION SCIENCE, 2022, 196
  • [37] Interfacial characteristics in multi-material laser powder bed fusion of CuZr/316L stainless steel
    Chueh, Yuan-Hui
    Hsieh, Bing-Yen
    Shih, Albert J.
    CIRP ANNALS-MANUFACTURING TECHNOLOGY, 2024, 73 (01) : 145 - 148
  • [38] Formation mechanism of MnS inclusion during heat treatments and its influence on the pitting behavior of 316L stainless steel fabricated by laser powder bed fusion
    Duan, Zhiwei
    Man, Cheng
    Cui, Hongzhi
    Cui, Zhongyu
    Wang, Xin
    CORROSION COMMUNICATIONS, 2022, 7 : 12 - 22
  • [39] Formation mechanism of MnS inclusion during heat treatments and its influence on the pitting behavior of 316L stainless steel fabricated by laser powder bed fusion
    Zhiwei Duan
    Cheng Man
    Hongzhi Cui
    Zhongyu Cui
    Xin Wang
    Corrosion Communication, 2022, 7 (03) : 12 - 22
  • [40] Formation mechanism of MnS inclusion during heat treatments and its influence on the pitting behavior of 316L stainless steel fabricated by laser powder bed fusion
    Zhiwei Duan
    Cheng Man
    Hongzhi Cui
    Zhongyu Cui
    Xin Wang
    Corrosion Communications, 2022, 7 (03) : 12 - 22