Preparation, characterization and kinetics studies of mesoporous silica from alkali dissolution of kaolinite

被引：2

作者：

Ibrahim, Abdullah S. ^{[1
]}

Baba, Alafara A. ^{[2
]}

机构：

[1] Fed Polytech Ayede, Dept Sci Lab Technol, PMB 4001, Ayede, Oyo State, Nigeria

[2] Univ Ilorin, Dept Ind Chem, PMB 1515, Ilorin 240003, Nigeria

来源：

CHEMICAL DATA COLLECTIONS | 2023年 / 45卷

关键词：

Thermal activated kaolinite; Mesoporous silica; Characterization; Sodium hydroxide; Kinetics; SURFACE-AREA; MINERALS; CATALYST; WASTE;

D O I：

10.1016/j.cdc.2023.101021

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

In search of cheaper and ecologically friendly material for porous silica preparation, thermal activated kaolinite was subjected to alkaline dissolution using NaOH solution. The result showed experimental reaction parameters such as alkali concentration, reaction temperature and liquid/ solid ratio affected the rate of silica extraction. At optimized condition, silica extraction reached 54.2% with apparent activation energy of 14.43 kJ/mol. The porous product was characterized by XRF, XRD, SEM, TEM and N2 adsorption-desorption. The product was amorphous with silica agglomerates. The pore size distribution by the BJH method was mesoporous with specific surface area of 10.36 m2/g and pore size of about 10.43 nm at maximum probability.

引用

页数：7

共 24 条

[11] One pot fusion route for the synthesis of zeolite 4A using kaolin [J].

Kirdeciler, Salih Kaan ;

Akata, Burcu .

ADVANCED POWDER TECHNOLOGY, 2020, 31 (10) :4336-4343

[12] The properties of amorphous nano-silica synthesized by the dissolution of olivine [J].

Lazaro, A. ;

Brouwers, H. J. H. ;

Quercia, G. ;

Geus, J. W. .

CHEMICAL ENGINEERING JOURNAL, 2012, 211 :112-121

[13] Kinetics of Vanadium Leaching from a Spent Industrial V2O5/TiO2 Catalyst by Sulfuric Acid [J].

Li, Qichao ;

Liu, Zhenyu ;

Liu, Qingya .

INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 2014, 53 (08) :2956-2962

[14] Template-free synthesis of kaolin-based mesoporous silica with improved specific surface area by a novel approach [J].

Li, Tiantian ;

Shu, Zhu ;

Zhou, Jun ;

Chen, Yun ;

Yu, Dongxue ;

Yuan, Ximing ;

Wang, Yanxin .

APPLIED CLAY SCIENCE, 2015, 107 :182-187

[15] Porous Materials from Thermally Activated Kaolinite: Preparation, Characterization and Application [J].

Luo, Jun ;

Jiang, Tao ;

Li, Guanghui ;

Peng, Zhiwei ;

Rao, Mingjun ;

Zhang, Yuanbo .

MATERIALS, 2017, 10 (06)

[16] Preparation of microporous silica from metakaolinite by selective leaching method [J].

Okada, K ;

Shimai, A ;

Takei, T ;

Hayashi, S ;

Yasumori, A ;

MacKenzie, KJD .

MICROPOROUS AND MESOPOROUS MATERIALS, 1998, 21 (4-6) :289-296

[17] Dissolution of aluminosilicate minerals and by-products in alkaline media [J].

Panagiotopoulou, Ch. ;

Kontori, E. ;

Perraki, Th. ;

Kakali, G. .

JOURNAL OF MATERIALS SCIENCE, 2007, 42 (09) :2967-2973

[18] Synthesis and characterization of amorphous precipitated silica from alkaline dissolution of olivine [J].

Raza, Nadeem ;

Raza, Waseem ;

Madeddu, Silvia ;

Agbe, Henry ;

Kumar, R. V. ;

Kim, Ki-Hyun .

RSC ADVANCES, 2018, 8 (57) :32651-32658

[19] The effects of carboxylic acid addition on hydrofluoric acid autoclave leaching of a ferrocolumbite [J].

Rodriguez, M ;

Rivarola, J ;

Ruiz, MD .

HYDROMETALLURGY, 2004, 74 (1-2) :39-46

[20] Mesoporous silica derived from kaolin: Specific surface area enlargement via a new zeolite-involved template-free strategy [J].

Shu, Zhu ;

Li, Tiantian ;

Zhou, Jun ;

Chen, Yun ;

Sheng, Zimo ;

Wang, Yanxin ;

Yuan, Ximing .

APPLIED CLAY SCIENCE, 2016, 123 :76-82

← 1 2 3 →