Effect of heat treatment on the microstructure and properties of CuCrZr prepared by laser powder bed fusion

被引：5

作者：

Chen, Xingfu ^{[1
,2
,3
]}

Dong, Peng ^{[4
]}

Zeng, Yong ^{[1
,2
,3
]}

Yao, Haihua ^{[1
,2
,3
]}

Chen, Jimin ^{[1
,2
,3
]}

机构：

[1] Beijing Univ Technol, Fac Mat & Mfg, Beijing 100124, Peoples R China

[2] Beijing Engn Res Ctr 3D Printing Digital Med Hlth, Beijing 100124, Peoples R China

[3] Minist Educ, Key Lab Transscale Laser Mfg Technol, Beijing 100124, Peoples R China

[4] Capital Aerosp Machinery Corp, Beijing 100076, Peoples R China

来源：

MATERIALS CHARACTERIZATION | 2024年 / 214卷

关键词：

Laser powder bed fusion; Copper alloy; Mechanical properties; Thermal conductivity; Heat treatment; ALLOY; EVOLUTION;

D O I：

10.1016/j.matchar.2024.114103

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this paper, CuCrZr alloys were prepared by laser powder bed fusion technique. Under optimum forming process conditions, a relative density of 99.7% was obtained and the specimens were analyzed for microstructure and properties. To enhance the mechanical properties of the copper alloy, the specimens are post-treated using both solution aging and direct aging heat treatments. The variation and influence mechanism of microstructure and mechanical properties, thermal conductivity and electrical conductivity were studied and analyzed. With direct aging heat treatment a large number of Cr nanoprecipitates can be obtained, significantly improving the properties of the alloy. The best synthesis properties obtained at an aging temperature of 450 degrees C were: microhardness 168.7 +/- 3.1 HV, ultimate tensile strength 481.7 +/- 7.6 MPa, electrical conductivity 73.9 +/- 0.9 %IACS, thermal conductivity 314.3 +/- 5.3 W/(m center dot K).