Magnesium aluminate spinel transparent ceramics with high optical and mechanical performance by Y3Al5O12 sintering additive

被引：1

作者：

Luo, Haoming ^{[1
,2
]}

Han, Dan ^{[1
]}

Zhang, Jian ^{[1
,2
]}

Wang, Shiwei ^{[1
,2
]}

机构：

[1] Chinese Acad Sci, Shanghai Inst Ceram, State Key Lab High Performance Ceram & Superfine M, Shanghai 200050, Peoples R China

[2] Univ Chinese Acad Sci, Ctr Mat Sci & Optoelect Engn, Beijing, Peoples R China

来源：

JOURNAL OF THE AMERICAN CERAMIC SOCIETY | 2024年 / 107卷 / 09期

基金：

中国国家自然科学基金;

关键词：

additive; optical properties; spinel; transparent ceramics; YAG; DOPED MGAL2O4 SPINEL; MICROSTRUCTURE; QUALITY; DENSIFICATION;

D O I：

10.1111/jace.19923

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

High-quality magnesium aluminate spinel (MAS) transparent ceramics were successfully fabricated using Y3Al5O12 (YAG) as the sintering additive. The influence of the YAG content on the sintering behavior, microstructure, and optical properties of the MAS transparent ceramics was systematically investigated. A 4 mm-thick sample with 0.01 wt.% YAG hot isostatic pressed at 1600 degrees C achieved the highest in-line transmittance of 84.0% at 400 nm and the flexural strength of the sample was as high as 347.3 MPa, which represents the highest-performing reported MAS transparent ceramics that were sintered with oxide additives.

引用

收藏

页码：6224 / 6232

页数：9

相关论文

共 40 条

[1] Rugged Spinel Windows and Optics for Harsh Environments [J].

Bayya, Shyam ;

Villalobos, Guillermo ;

Kim, Woohong ;

Busse, Lynda ;

Sanghera, Jasbinder .

PHOTONIC APPLICATIONS FOR AEROSPACE, COMMERCIAL, AND HARSH ENVIRONMENTS IV, 2013, 8720

[2] Transparent ceramic and glass-ceramic materials for armor applications [J].

Benitez, Tobias ;

Gomez, Sergio Y. ;

Novaes de Oliveira, Antonio Pedro ;

Travitzky, Nahum ;

Hotza, Dachamir .

CERAMICS INTERNATIONAL, 2017, 43 (16) :13031-13046

[3] Influence of graphite contamination on the optical properties of transparent spinel obtained by spark plasma sintering [J].

Bernard-Granger, G. ;

Benameur, N. ;

Guizard, C. ;

Nygren, M. .

SCRIPTA MATERIALIA, 2009, 60 (03) :164-167

[4]

BernardGranger G., 2010, SINTERED PRODUCT CUB

[5] Fifty Years of Research and Development Coming to Fruition; Unraveling the Complex Interactions during Processing of Transparent Magnesium Aluminate (MgAl2O4) Spinel [J].

du Merac, Marc Rubat ;

Kleebe, Hans-Joachim ;

Mueller, Mathis M. ;

Reimanis, Ivar E. .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2013, 96 (11) :3341-3365

[6] Effect of Impurities and LiF Additive in Hot-Pressed Transparent Magnesium Aluminate Spinel [J].

du Merac, Marc Rubat ;

Reimanis, Ivar E. ;

Smith, Charlene ;

Kleebe, Hans-Joachim ;

Mueller, Mathis M. .

INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2013, 10 :E33-E48

[7] A thermodynamic approach to obtaining transparent spinel (MgAl2O4) by hot pressing [J].

Esposito, Laura ;

Piancastelli, Andreana ;

Miceli, Patrizia ;

Martelli, Stefano .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2015, 35 (02) :651-661

[8] Mechanical and optical properties of MgAl2O4 ceramics and ballistic efficiency of spinel based armour [J].

Gajdowski, Caroline ;

D'Elia, Raffaele ;

Faderl, Norbert ;

Bohmler, Judith ;

Lorgouilloux, Yannick ;

Lemonnier, Sebastien ;

Leriche, Anne .

CERAMICS INTERNATIONAL, 2022, 48 (13) :18199-18211

[9]

Gilde G., 2006, ARMY RES LAB ABERDEE, V6

[10] Transparent Ceramics at 50: Progress Made and Further Prospects [J].

Goldstein, Adrian ;

Krell, Andreas .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2016, 99 (10) :3173-3197

← 1 2 3 4 →