Improved Joint Formation and Ductility during Electron-Beam Welding of Ti6Al4V and Al6082-T6 Dissimilar Alloys

The current work is based on investigating the influence of different technological conditions of electron-beam welding on the microstructure and mechanical properties of joints between Ti6Al4V and Al6082-T6 dissimilar alloys. The plates were in all cases preheated to 300 degrees C. Different strategies of welding were investigated such as varying the electron-beam current/welding speed ratio (Ib/vw) and applying a beam offset towards the aluminum side. The heat input during the experiments was varied in order to guarantee full penetration of the electron beam. The macrostructure of the samples was studied, and the results indicated that using a high beam power and a high welding speed leads to an increased formation of defects within the structure of the weld seam. Utilizing a lower beam current along with a lower welding speed leads to the stabilization of the electron-beam welding process and thus to the formation of an even weld seam with next to no defects and high ductility. Using this approach gave the highest ultimate tensile strength (UTS) of 165 MPa along with a yield strength (YS) of 80 MPa and an elongation (epsilon) figure of 18.4%. During the investigation, improved technological conditions of electron-beam welding of Ti6Al4V and Al6082-T6 dissimilar alloys were obtained, and the results were discussed regarding possible practical applications of the suggested approach along with its scientific contribution to developing further strategies for electron-beam welding of other dissimilar alloys. The downsides and the economic effect of the presented method for welding Ti6Al4V and Al6082-T6 were also discussed.