Low-Cycle Fatigue Performance and Fracture Mechanism of Nickel-based Single Crystal Superalloy at 530 °C

被引：0
|
作者：
Zhang, Jingang [1 ,2 ]
Chen, Xing [1 ,2 ]
Li, Zhen [1 ,2 ]
Tian, Fuzheng [1 ,2 ]
Liu, Xinling [1 ,2 ]
机构：
[1] Failure Analysis Center of Aero Engine Corporation of China, AECC Beijing Institute of Aeronautical Materials, Beijing,100095, China
[2] Beijing Key Laboratory of Aeronautical Materials Testing and Evaluation, Beijing,100095, China
来源：
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering | 2023年 / 52卷 / 06期
关键词：
Compendex;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Low-cycle fatigue
引用
收藏
页码：1985 / 1993
相关论文
共 50 条
  • [31] Low Cycle Fatigue/Corrosion Interactions at 950 °C of AM1 Single Crystal Nickel-Based Superalloy
    Martin, A.
    Drouelle, E.
    Rame, J.
    Cormier, J.
    Pedraza, F.
    HIGH TEMPERATURE CORROSION OF MATERIALS, 2024, 101 (05) : 961 - 970
  • [32] Damage-based low-cycle fatigue lifetime prediction of nickel-based single-crystal superalloy considering anisotropy and dwell types
    Zhang, Bin
    Wang, Rongqiao
    Hu, Dianyin
    Jiang, Kanghe
    Hao, Xinyi
    Mao, Jianxing
    Jing, Fulei
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2020, 43 (12) : 2956 - 2965
  • [33] Effect of Local Recrystallized Grains on the Low Cycle Fatigue Behavior of a Nickel-Based Single Crystal Superalloy
    Ma, Xianfeng
    Jiang, Jishen
    Zhang, Wenjie
    Shi, Hui-ji
    Gu, Jialin
    CRYSTALS, 2019, 9 (06):
  • [34] Fatigue Fracture Mechanism of a Nickel-Based Single Crystal Superalloy with Partially Recrystallized Grains at 550 °C by In Situ SEM Studies
    Yang, Hao
    Jiang, Jishen
    Wang, Zhuozheng
    Ma, Xianfeng
    Tu, Jiajun
    Shi, Hui-ji
    Zhai, Hailin
    Zhang, Wenjie
    METALS, 2020, 10 (08) : 1 - 11
  • [35] Comparison of low-cycle fatigue behaviors between two nickel-based single-crystal superalloys
    Li, P.
    Li, Q. Q.
    Jin, T.
    Zhou, Y. Z.
    Li, J. G.
    Sun, X. F.
    Zhang, Z. F.
    INTERNATIONAL JOURNAL OF FATIGUE, 2014, 63 : 137 - 144
  • [36] Directional γ-γ prime coarsening in a monocrystalline nickel-based superalloy during low-cycle thermomechanical fatigue
    Friedrich-Alexander Universitat Erlangen-Nurnberg Institut fur Werkstoffwissenschaften, Allgemeine Werkstoffeigenschaften - Martensstrasse 5, 91058 Erlangen, Germany
    Scr Metall Mater, 3 (411-416):
  • [37] Very High Cycle Fatigue Properties of a Coated Nickel-Based Single Crystal Superalloy
    Morales, Antonio Vicente
    Mauget, F.
    Caradec, A.
    Larrouy, B.
    Villechaise, P.
    Cormier, J.
    SUPERALLOYS 2024, ISS 2024, 2024, : 617 - 625
  • [38] The low-cycle fatigue behavior and an entropy-based life prediction model for Nickel-based single crystal superalloy across an extensive temperature range
    Wang, Jundong
    Yang, Leike
    Lian, Yeda
    Wen, Zhixun
    Lu, Hao
    Ma, Zhuobin
    Yue, Zhufeng
    ENGINEERING FRACTURE MECHANICS, 2024, 301
  • [39] Effect of Warm Laser Shock Peening on the Low-Cycle Fatigue Behavior of DD6 Nickel-Based Single-Crystal Superalloy
    Tang, Zhanghan
    Wang, Kedian
    Dong, Xia
    Duan, Wenqiang
    Mei, Xuesong
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2021, 30 (04) : 2930 - 2939
  • [40] Effect of Warm Laser Shock Peening on the Low-Cycle Fatigue Behavior of DD6 Nickel-Based Single-Crystal Superalloy
    Zhanghan Tang
    Kedian Wang
    Xia Dong
    Wenqiang Duan
    Xuesong Mei
    Journal of Materials Engineering and Performance, 2021, 30 : 2930 - 2939
12345