Preparation and bioactivity of biodegradable β-tricalcium phosphate / calcium carbonate / phosphate bioactive glass composite porous ceramic

被引：1
作者：
Chen W. [1 ]
Liu Y. [1 ]
Zhu J. [1 ]
Zhou M. [1 ]
Chen X. [1 ]
机构：
[1] Department of Biomedical Engineering, Guangzhou Medical University, Guangzhou
[2] Stomatology Hospital of Guangzhou Medical University, Guangzhou
来源：
Journal of Applied Biomaterials and Functional Materials | 2019年 / 17卷 / 02期
基金：
中国国家自然科学基金;
关键词：
biocompatibility; biodegradation; phosphate bioactive glass; porous ceramics;
D O I：
10.1177/2280800019847071
中图分类号：
学科分类号：
摘要：
Background: At present, scaffold biomaterials with great biodegradation and biocompatibility are attracting more and more attention. Phosphate bioactive glass (PBG) without Si has been prepared successfully, with a glass transition temperature below 600°C. Calcium carbonate (CC)-based bioceramics with PBG as binder were sintered rapidly at a lower temperature. β-Tricalcium phosphate (β-TCP) has always been used to synthesize clinical ceramics due to its wonderful biocompatibility. Here, we combined the advantages of these raw materials to obtain a novel β-TCP/CC/PBG composite porous ceramic. Method: The preparation process of β-TCP/CC/PBG was optimized by controlling PBG content, NaCl ratio, sintering temperature, and holding time. Ceramic biodegradability was evaluated by soaking in a Tris-HCl buffer in vitro, and biocompatibility of the new material was indicated using CCK-8 tests and a live/dead fluorescence assay. Results: The best mechanical properties of β-TCP/CC/PBG composite porous ceramics were obtained with a PBG content of 60%, at which point the proportion of NaCl exerted the most significant influence on the density, porosity, and mechanical properties of the materials. The weight loss rate of the composite ceramics was 11.30%, which was much higher than that of β-TCP (1.41%) and hydroxyapatite (0.83%) ceramics. CCK-8 test and live/dead fluorescence assay indicated that the composite porous ceramics showed a biocompatibility similar to that of β-TCP ceramics. Conclusion: β-TCP/CC/PBG composite porous ceramics have potential applications in bone regeneration. It is hoped that the novel biomaterial developed in this study will prove useful for the repair of bone defects. © The Author(s) 2019.
引用
收藏
相关论文
共 28 条
  • [1] Saiz E., Boccaccini A.R., Chevalier J., Et al., Editorial on bioceramics for bone repair, J Eur Ceram Soc, 38, 3, pp. 821-822, (2018)
  • [2] Yuan H., De Bruijn J.D., Li Y., Et al., Bone formation induced by calcium phosphate ceramics in soft tissue of dogs: a comparative study between porous alpha-TCP and beta-TCP, J Mater Sci Mater Med, 12, 1, pp. 7-13, (2001)
  • [3] Palmer I., Nelson J., Schatton W., Et al., Biocompatibility of calcium phosphate bone cement with optimised mechanical properties: an in vivo study, J Mater Sci Mater Med, 27, 12, (2016)
  • [4] Szponder T., Mytnik E., Jaegermann Z., Use of calcium sulfate as a biomaterial in the treatment of bone fractures in rabbits—Preliminary studies, Bull Vet Inst Pulawy, 57, 1, pp. 119-122, (2013)
  • [5] Bui X.V., Synthesis and characterization of HA/β-TCP bioceramic powder, Vietnam J Chem, 56, 2, pp. 152-155, (2018)
  • [6] Ku K.L., Grondahl L., Hui D., In vitro degradation study of polyanhydride copolymers/surface grafted hydroxyapatite composites for bone tissue application, Polym Degrad Stab, 140, pp. 136-146, (2017)
  • [7] Du M., Kuang Z., Ji H., Mao K., Enhanced degradation and osteogenesis of β-tricalcium phosphate/calcium sulfate composite bioceramics: The effects of phase ratio, J Biomater Tissue Eng, 4, 5, pp. 389-398, (2014)
  • [8] Hao F., Qin L., Liu J., Et al., Assessment of calcium sulfate hemihydrate-tricalcium silicate composite for bone healing in a rabbit femoral condyle model, Mater Sci Eng C, 88, pp. 53-60, (2018)
  • [9] Guillemin G., Patat J.L., Fournie J., Et al., The use of coral as a bone graft substitute, J Biomed Mater Res, 21, 5, pp. 557-567, (1987)
  • [10] Martina M., Subramanyam G., Weaver J.C., Et al., Developing macroporous bicontinuous materials as scaffolds for tissue engineering, Biomaterials, 26, 28, pp. 5609-5616, (2005)
123