Self-Healing Performance of Cement-Based Materials Mixed with Magnesium Acrylate

被引：0

作者：

Li F. ^{[1
]}

Gao H. ^{[1
]}

Jiang Y. ^{[1
]}

Wen T. ^{[1
]}

Wang J. ^{[1
]}

Yu Y. ^{[1
]}

机构：

[1] School of Civil Engineering, Southwest Jiaotong University, Chengdu

来源：

Xinan Jiaotong Daxue Xuebao/Journal of Southwest Jiaotong University | 2022年 / 57卷 / 05期

关键词：

cement-based materials; EIS; magnesium acrylate; self-healing; SEM;

D O I：

10.3969/j.issn.0258-2724.20200487

中图分类号：

学科分类号：

摘要：

The self-healing performance of cement mortar specimens at different ages and temperatures was tested by compressive strength repair rate, crack repair rate, and electrochemical impedance spectroscopy (EIS), and then was analyzed using the scanning electronic microscope (SEM) to study the microscopic self-healing mechanism of magnesium acrylate cement-based materials. The test results showed that the effect of magnesium acrylate on the compressive strength repair and apparent repair of the mortar specimens was not obvious at the early age. The effect on compressive strength repair intensifies gradually with the increasing age, and the apparent crack repair rate at 7 d reached 100.0%. Meanwhile, medium-high temperature was beneficial to self-healing effect, but the effect above 40 ℃ was no longer significant. EIS showed that the equivalent circuit parameters of the test group at the age of 28 d were better than those of the control group; the repair effect of the magnesium acrylate at old age is significantly better than the healing" effect brought by the hydration reaction of cement-based materials. © 2022 Science Press. All rights reserved."

引用

页码：1055 / 1062

页数：7

共 24 条

[1]

ZHANG Peng, FENG Jingjing, CHEN Wei, Et al., Self-healing performance of concrete： a technological review, Materials Review, 32, 19, pp. 3375-3386, (2018)

[2]

pp. 18-19, (2018)

[3]

(2018)

[4]

(2018)

[5]

(2015)

[6]

XING Feng, NI Zhuo, TANG Jiaoning, Et al., State-of-the-art for self-healing concrete[J], Journal of Shenzhen University (Science and Engineering), 30, 5, pp. 486-494, (2013)

[7]

DRY C., Alteration of matrix permeability and associated pore and crack structure by the time release of internal chemicals [C], Proceedings of Advance in Cementitious Materials, pp. 729-768, (1990)

[8]

DRY C., Matrix cracking repair and filling using active and passive modes for smart timed release of chemicals from fibers into cement matrices[J], Smart Materials and Structures, 3, 2, pp. 118-123, (1994)

[9]

DRY C，, MCMILLAN W., Three-part methylmethacrylate adhesive system as an internal delivery system for smart responsive concrete[J], Smart Materials and Structures, 5, 3, pp. 297-300, (1996)

[10]

DRY C M., Three designs for the internal release of sealants, adhesives, and waterproofing chemicals into concrete to reduce permeability, Cement and Concrete Research, 30, 12, pp. 1969-1977, (2000)

← 1 2 3 →