Investigation on the early proceeding of cement hydration containing dispersed nano Calcium Silicate Hydrated (CSH) seeds

Steam curing process is a traditional method for accelerating the progression of cement hydration to satisfy the rapid development of compressive strength in precast concrete industry. However, steam curing would release significant amount of CO 2 into the atmosphere. In order to avoid the serious environmental pollution caused by the steam curing process, Calcium Silicate Hydrate (CSH) dispersed by comb -like polycarboxylate superplasticizer (PCE), shorted as dispersed nano CSH seed, was utilized to promote the early cement hydration at normal temperature. This investigation aims at disclosing the hydration process of cement and the microstructure evolution of cement paste in the presence of dispersed nano CSH seed during the early stage via setting time, ultrasonic pulse velocity (UPV), compressive strength, conductivity, pH, thermogravimetric (TG), 29 Si NMR and nitrogen adsorption/desorption. The results demonstrated that with the dispersed nano CSH seed increasing, the setting process of cement paste was shortened dramatically, the compressive strength and UPV of cement mortar increased significantly especially at 12 h. The variation of conductivity and pH of cement suspension indicated that the ion dissolution process was promoted by dispersed nano CSH seed, which therefore conducive to the precipitation of cement hydration products. TG curves exhibited that the formation of cement hydration products, including CH (Calcium Hydrated), AFt and CSH gel were accelerated by dispersed nano CSH seed. The 29 Si NMR (Nuclear Magnetic Resonance) and nitrogen adsorption/desorption results validated that the incorporating dispersed nano CSH seed promoted considerably the polymerization of CSH gel. The aforementioned results are correlated well with the fast formation of microstructure and in turn the rapid development of compressive strength at early age.