Fatigue crack growth behavior of 7050 aluminum alloy friction stir welded joint

被引：0

作者：

Jin Y. ^{[1
,2
]}

Zhang L. ^{[1
]}

Wang X. ^{[1
]}

机构：

[1] Lanzhou University of Technology, Lanzhou

[2] State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou

来源：

Hanjie Xuebao/Transactions of the China Welding Institution | 2020年 / 41卷 / 10期

关键词：

7050 aluminum alloy; Fatigue crack growth rate; Fatigue fracture; Friction stir welding;

D O I：

10.12073/j.hjxb.20200709002

中图分类号：

学科分类号：

摘要：

The fatigue crack growth behavior of 5 mm thick 7050 aluminum alloy friction stir welding joints in different areas was analyzed and studied. The results show that the fatigue crack growth rate is the fastest in the weld nugget zone. The second is the position of the thermo-mechanically affected zone of advancing side. The fatigue crack growth rate is the slowest in the thermo-mechanically affected zone of retreating side. The fatigue crack is propagated by intergranular and transgranular mixing in the weld nugget zone, while the crack is propagated by transgranular in the thermo-mechanically affected zone. The deflection of the crack and the generation of the crack branch will reduce the fatigue crack growth rate. In the initial stage of fatigue crack growth, the fracture surface of the weld nugget zone is distributed with grain size fracture planes, and fatigue striations are generated; fatigue striations did not occur in the thermo-mechanically affected zone, but tire indentation patterns appear here. During the steady-state propagation of fatigue crack, the crack growth rate increased, and fatigue striations appeared in the weld nugget zone and the thermo-mechanically affected zone, and secondary cracks were generated. Copyright © 2020 Transactions of the China Welding Institution. All rights reserved.

引用

页码：11 / 16

页数：5

共 10 条

[1]

Jin Yuhua, Huo Renjie, Li Changfeng, Et al., Influence of ratational speed on fracture characteristics of 7055 aluminum alloy friction stir weld joints, Transactions of the China Welding Institution, 38, 2, pp. 10-13, (2017)

[2]

Tra Tran Hung, Okazaki Masakazu, Suzuki Kenji, Fatigue crack propagation behavior in friction stir welding of AA6063-T5: Roles of residual stress and microstructure, International Journal of Fatigue, 43, pp. 23-29, (2012)

[3]

Wang Xijing, Li Shuwei, Niu Yong, Et al., Fatigue crack growth rate of A7075FSW, Transactions of the China Welding Institution, 29, 9, pp. 5-7, (2008)

[4]

Zou B L, Yang X Q, Chen J H., Fatigue crack growth rates in friction stir welding joints of 7075-T6 Al alloy and fatigue life prediction based on AFGROW, Advanced Materials Research, 337, pp. 507-510, (2011)

[5]

Shou W B, Yi D Q, Liu H Q, Et al., Effect of grain size on the fatigue crack growth behavior of 2524-T3 aluminum alloy, Archives of Civil and Mechanical Engineering, 16, 3, pp. 304-312, (2016)

[6]

Wang Xijing, Li Na, Zhang Zhongke, Et al., FSW residual stress of aluminum alloy LY12, Transactions of the China Welding Institution, 33, 9, pp. 81-84, (2012)

[7]

Jian Haigen, Jiang Feng, Zheng Xiuyuan, Et al., EBSD analysis of propagation behaviour of fatigue cracks in high strength aluminum alloy, Transactions of Materials and Heat Treatment, 32, 2, pp. 75-80, (2011)

[8]

Wang Ping, Liang Tian, Hou Shiyao, Et al., Micromechanism of short crack initiation and propagation in Ti-153 alloy, Journal of Northeastern University(Natural Science), 29, 12, pp. 1711-1714, (2008)

[9]

Huang Shu, Investigation of laser peening on the fatigue crack growth properties and life extension mechanism of 6061-T6 aluminum alloy, (2012)

[10]

Wang Yilin, Pan Qinglin, Wei Lili, Et al., Fatigue fracture characteristic of 7050-T7451 high-strength aluminum alloy thick plate, Materials for Mechanical Engineering, 37, 6, pp. 26-30, (2013)

← 1 →