Unsteady Thermal Stresses of Thermal Barrier Coatings under Cyclic Heating

被引:0
作者
Suzuki K. [1 ]
Toyokawa H. [2 ]
Saji C. [2 ]
Yamazaki Y. [3 ]
Okumura T. [4 ]
机构
[1] Faculty of Education, Niigata University, Nishi-ku, Niigata
[2] Japan Synchrotron Radiation Research Institute, Sayo-gun, Hyogo
[3] Faculty of Engineering, Chiba University, Inage-ku, Chiba
[4] Graduate School of Engineering, Chiba University, Inage-ku, Chiba
基金
日本学术振兴会;
关键词
Heat cycle; Synchrotron radiations; Thermal barrier coating; Unsteady thermal stress; X-ray stress measurement;
D O I
10.2472/JSMS.72.821
中图分类号
学科分类号
摘要
The thermal stresses of the thermal barrier coatings (TBCs) under cyclic heating were measured using hard synchrotron X-rays of 70 keV at the beam line BL02B1 in SPring-8. We were able to quickly measure the unsteady stresses using the CdTe pixel detector which is an area detector. The two kinds of the TBC specimens were prepared. One was made by atmosphere plasma spraying (APS) and the other was made by suspension plasma spraying (SPS). The steady thermal stresses in both the APS and SPS specimens showed the same value during the heating and cooling processes. Therefore, the steady thermal stresses were caused by the miss match of the thermal expansions. The unsteady thermal stresses were larger than the steady stresses in both the APS and the SPS specimens. The unsteady thermal stresses also include the stress caused by the temperature gradient. According to the behavior of the unsteady thermal stresses measured, the thermal stress of the APS top coat did not exceed 100 MPa due to non-elastic deformation an sliding effect of lamella structure. For the SPS specimen, it was found that the tensile and compressive stresses were relaxed due to the columnar structure. © 2023 The Society of Materials Science, Japan.
引用
收藏
页码:821 / 827
页数:6
相关论文
共 50 条
[41]   Damage Grading Evaluation of Thermal Barrier Coatings under CMAS Corrosion [J].
Liu, Wei ;
Liu, Yangguang ;
Wang, Weize ;
Yang, Ting ;
Zhang, Wenkang ;
Liu, Chen ;
Zhang, Chengcheng ;
Tu, Shantung .
COATINGS, 2023, 13 (09)
[42]   Interface failure analysis of thermal barrier coatings under CMAS penetration [J].
Zhang Z. ;
Han Y. ;
Wang W. ;
Cai Z. .
Hangkong Dongli Xuebao/Journal of Aerospace Power, 2021, 36 (08) :1702-1711
[43]   Performance of thermal barrier coatings on γ-TiAl [J].
Braun, R ;
Leyens, C ;
Fröhlich, A .
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2005, 56 (12) :930-936
[44]   Thermal Barrier Coatings: Evolution and Perspectives [J].
Camello Limar, Carlos Roberto .
SOLDAGEM & INSPECAO, 2014, 19 (04) :353-363
[45]   Toughening Mechanism of Thermal Barrier Coatings [J].
Chen, Yuhui ;
Zhang, Ruolin ;
Zhang, Guoshuai ;
Jiang, Pengyang ;
Song, Jun ;
Chu, Xiaowan .
INTERNATIONAL JOURNAL OF THERMOPHYSICS, 2021, 42 (05)
[46]   Modifications of thermal barrier coatings (TBCs) [J].
Schmitt-Thomas, KG ;
Haindl, H ;
Fu, D .
SURFACE & COATINGS TECHNOLOGY, 1997, 94-5 (1-3) :149-154
[47]   Failure aspects of thermal barrier coatings [J].
Singheiser, L ;
Steinbrech, R ;
Quadakkers, WJ ;
Herzog, R .
MATERIALS AT HIGH TEMPERATURES, 2001, 18 (04) :249-259
[48]   Interface science of thermal barrier coatings [J].
Theodore M. Besmann .
Journal of Materials Science, 2009, 44 :1661-1663
[49]   Toughening Mechanism of Thermal Barrier Coatings [J].
Yuhui Chen ;
Ruolin Zhang ;
Guoshuai Zhang ;
Pengyang Jiang ;
Jun Song ;
Xiaowan Chu .
International Journal of Thermophysics, 2021, 42
[50]   The effect of the type of thermal exposure on the durability of thermal barrier coatings [J].
Kim, GM ;
Yanar, NM ;
Hewitt, EN ;
Pettit, FS ;
Meier, GH .
SCRIPTA MATERIALIA, 2002, 46 (07) :489-495