Research Progress on Corrosion Fatigue Behavior of Biomedical Degradable Magnesium-Based Alloys

被引：0

作者：

Chen, Liansheng ^{[1
]}

Zheng, Yaqi ^{[1
]}

Zhang, Yuan ^{[1
]}

Liu, Yun ^{[1
]}

Li, Jingyuan ^{[2
]}

Tian, Yaqiang ^{[1
]}

Zheng, Xiaoping ^{[1
]}

机构：

[1] Key Laboratory of the Ministry of Education for Modern Metallurgy Technology, North China University of Science and Technology, Tangshan,063210, China

[2] School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing,100083, China

来源：

Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering | 2021年 / 50卷 / 09期

关键词：

Magnesium alloys - Corrosion resistant alloys - Degradation - Atmospheric corrosion - Corrosion rate - Fracture - Fatigue crack propagation - Corrosion resistance - Mechanisms;