Properties and microstructure of 45 steel surface processed by electron beam micro melting polishing

被引：0
作者：
Wang R. [1 ]
Wang Y. [2 ]
Cui Y. [1 ]
Li S. [1 ]
机构：
[1] Guilin University of Electronic Technology, Guilin
[2] Huizhou College, Huizhou
来源：
Hanjie Xuebao/Transactions of the China Welding Institution | 2019年 / 40卷 / 05期
关键词：
45; steel; Electron beam; Microstructure; Polishing; Surface roughness;
D O I：
10.12073/j.hjxb.2019400137
中图分类号：
学科分类号：
摘要：
Process the surface of 45 steel was carried out in order to significantly improve the surface roughness and comprehensive mechanical properties of 45 steel using electron beam micro melting polishing technology. The influences of electron beam polishing on surface roughness, microstructure and hardness of the modified layer were studied. The influences of electron beam scanning current and scanning speed on surface roughness and microstructure of modified layer was also discussed. The results show that the surface roughness of 45 steel reduced from 2.091 μm to 0.738 μm. The decrease rate is 64.7%. The surface modification layer can be divided into the polishing zone, the heat affected zone and the matrix zone. The microstructure of the polishing layer is acicular martensite with 950 ~ 913 HV hardness. The microstructure of the heat affected zone are acicular martensite and ferrite with 855 ~ 280 HV hardness. The microstructure of the matrix zone are pearlite and ferrite with a hardness of 244 ~ 204 HV. The influence of electron beam processing parameters on the surface roughness after polishing is significant. Under the corresponding polish effect condition, thickness of the modified layer increases with the increasing of the scanning current of electron beam, and decreases with the increasing of scanning speed. © 2019, Editorial Board of Transactions of the China Welding Institution, Magazine Agency Welding. All right reserved.
引用
收藏
页码：113 / 119
页数：6
相关论文
共 14 条
  • [1] Manladan S.M., Yusof F., Ramesh S., Et al., Microstructure and mechanical properties of resistance spot welded in welding-brazing mode and resistance element welded magnesium alloy/austenitic stainless steel joints, Journal of Materials Processing Technology, 250, pp. 45-54, (2017)
  • [2] Pan J., Ren R., Qi Z., Interface deformation and its role of steel 45 in vacuum diffusion welding, Transactions of the China Welding Institution, 31, 4, pp. 65-69, (2010)
  • [3] Li H.L., Liu D., Song Y.Y., Et al., Microstructure and mechanical properties of underwater wet welded highcarbon-equivalent steel Q460 using austenitic consumables, Journal of Materials Processing Technology, 249, pp. 149-157, (2017)
  • [4] Chang C.S., Yang K.S., Chung C.K., Et al., Surface quality, microstructure, and mechanical properties of the SKD 61 tool steel with prior heat treatment affected by single-and double-pass continuous wave laser polishing, The International Journal of Advanced Manufacturing Technology, 92, 1, pp. 1-16, (2017)
  • [5] Urlea V., Brailovski V., Electropolishing and electropolishing-related allowances for IN625 alloy components fabricated by laser powder-bed fusion, The International Journal of Advanced Manufacturing Technology, 92, 9-12, pp. 4487-4499, (2017)
  • [6] Dai W., Zheng Z., Li J., Et al., Latest development of metal surface polishing and surface modification with electron beam, Chinese Journal of Vacuum Science and Technology, 36, 5, pp. 582-596, (2016)
  • [7] Lu J., Wei D., Wang R., Et al., Surface polishing and modification of 3Cr2Mo mold steel by electron beam irradiation, Vacuum, 143, pp. 283-287, (2017)
  • [8] Uno Y., Okada A., Uemura K., Et al., A new polishing method of metal mold with large-area electron beam irradiation, Journal of Materials Processing Technology, 187, pp. 77-80, (2007)
  • [9] Wei D., Wang X., Wang R., Et al., Surface modification of 5CrMnMo steel with continuous scanning electron beam process, Vacuum, 149, pp. 118-123, (2018)
  • [10] Qu Y., Zhou J., Zhao L., Et al., Fiber laser remelting technology of 45 steel, Transactions of the China Welding Institution, 36, 7, pp. 59-63, (2015)
12