Influence of two-step aging on structure and stress corrosion sensitivity of friction stir welded 7050-T7451 aluminum alloys

被引：0
|
作者：
Zhang H. [1 ]
Guo Q. [1 ]
Zhao C. [1 ]
Lin S. [2 ]
Shi G. [3 ]
机构：
[1] Beijing Institute of Petrochemical Technology, Beijing
[2] State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin
[3] The Welding Institute, Cambridge
来源：
Hanjie Xuebao/Transactions of the China Welding Institution | 2020年 / 41卷 / 06期
关键词：
7050 aluminum alloy; Friction stir welding; Stress corrosion sensitivity; Two-step aging;
D O I：
10.12073/j.hjxb.20190513001
中图分类号：
学科分类号：
摘要：
3 mm thick 7050-T7451aluminum alloy joint was obtained by friction stir welding, and the two-stage aging treatment was performed at 121 ℃ × 5 h + 163 ℃ × 27 h after welding. Microstructure, hardness profiles and stress corrosion sensitivity of the joint were measured and studied. The results indicate that through the two-step aging, the grain size is coarsened, the age-hardening precipitates and PFZ become wider at the same time, which results in the discontinuous grain boundary; the microhardness of the FSW joints decreased, but the heat-affected zone significantly narrowed, which increased the uniformity of the microhardness of the FSW joints; and the two-stage aging effectively reduced the stress corrosion sensitivity of the FSW joints. The joints with aging treatment were not broken after 60 days, however all the joints without aging treatment were broken within 1 day. Copyright © 2020 Transactions of the China Welding Institution. All rights reserved.
引用
收藏
页码：1 / 5
页数：4
相关论文
共 18 条
  • [1] Zhang Xin, Han Dong, Wu Jun, Et al., Effect of postweld heat treatment on FSW joint of 7050 aluminum alloy, Aerospace Manufacturing Technology, 3, (2018)
  • [2] Wang Guojun, Wang Zhutang, Application of aluminum alloy in Chinese civil aircraft, Light Alloy Fabrication Technology, 45, 11, (2017)
  • [3] Geng Ziming, Song Jie, Wang Lei, Et al., Application status and prospect of friction stir welding, Welding Technology, 48, 1, (2019)
  • [4] Zhang Hua, Zhao Changyu, Lin Sanbao, Et al., Microstructure and properties of stationary shoulder FSW joint of 7050-T7451 aluminum alloy, Welding & Joining, 9, (2018)
  • [5] Jiang Baohua, Zhang Ping, Wang Limei, Et al., Effect of two-step aging on microstructure and mechanical properties of 7050 aluminum alloy, Ordnance Material Science and Engineering, 40, 3, pp. 56-58, (2017)
  • [6] Zhang Chengcong, Chang Baohua, Tao Jun, Et al., Influence factors of dynamic recrystallization of 7050 aluminium alloy friction stir weld, Transactions of the China Welding Institution, 33, 8, pp. 89-92, (2012)
  • [7] Brown Rebecca, Tang Wei, Reynolds A P., Multi-pass friction stir welding in alloy 7050-T7451: effects on weld response variables and on weld properties, Materials Science and Engineering: A, 513, pp. 115-121, (2009)
  • [8] Emilie B, Angeline P Q, Monique P, Et al., Relationship between microstructure, microhardness and corrosion sensitivity of an AA2024-T3 friction stir welded joint, Corrosion Science, 53, 9, pp. 3026-3034, (2011)
  • [9] Kun Zhang, Guohong Luan, Ruidong Fu, Effect of natural aging on microstructure and mechanical properties of friction stir welded 7050-T7451 joints[J], China Welding, 25, 3, (2016)
  • [10] Li Guowei, Chen Furong, Han Yongquan, Et al., Influence of post-weld heat treatment on microstructure and mechanical properties of 7075 aluminum alloy P-VPPA welded joint, Transactions of the China Welding Institution, 39, 2, pp. 57-60, (2018)
12