ASSESSMENT OF THE EFFECTIVENESS OF SELECTED COATINGS FOR PROTECTION AGAINST UV RADIATION IN GLASS FIBER REINFORCED COMPOSITES (GFRP)

被引：0

作者：

Smolen, Jakub ^{[1
]}

Bechcinska, Karolina ^{[2
]}

Smok, Weronika ^{[3
]}

Olesik, Piotr ^{[1
]}

Stepien, Krzysztof ^{[1
]}

机构：

[1] Silesian Tech Univ, Fac Mat Engn, Ul Z Krasinskiego 8, PL-40019 Katowice, Poland

[2] Lukasiewicz Inst Ceram & Bldg Mat, Ul Cementowa 8, PL-31983 Krakow, Poland

[3] Silesian Tech Univ, Fac Mech Engn, Ul S Konarskiego 18a, PL-44100 Gliwice, Poland

来源：

COMPOSITES THEORY AND PRACTICE | 2024年 / 24卷 / 01期

关键词：

GFRP; polymer composites; UV degradation; coatings; DEGRADATION;

D O I：

10.62753/ctp.2024.09.1.1

中图分类号：

TB33 [复合材料];

学科分类号：

摘要：

The paper describes the effectiveness of selected protective coatings against ultraviolet radiation in glass fiber reinforced composites. Epoxy resin matrix GFRP composites with 1 mm thick coatings were produced. Four types of coatings were compared: pure epoxy resin, epoxy resin with the addition of a UV stabilizer from the benzophenone group, epoxy resin with an addition of graphite (screening function) and a commercial polyester gelcoat. The composites were irradiated for 1000 h with ultraviolet radiation from three separate radiation ranges: UVA, UVB, UVC. The changes in the surface appearance, flexural strength and chemical structure were described. The results shows that UV radiation caused changes in the surface condition for the reference samples (coating without additives), such as yellowing and matting. Also, a reduction in the flexural strength by over 10% and changes in the chemical structure, mainly caused by oxidation processes and the cracking of chemical bonds were observed. The most beneficial protection was found to be the UV stabilizer from the benzophenone group, the addition of which provides UV protection over the entire radiation range and protects the material against negative changes in the coating's chemical structure. Also, similar results were obtained for the samples with the graphite coating.

引用

页码：65 / 71

页数：7

共 26 条

[1] THE PHOTO-STABILIZATION OF POLYPROPYLENE - A REVIEW
ALLEN, NS
CHIRINISPADRON, A
HENMAN, TJ
[J]. POLYMER DEGRADATION AND STABILITY, 1985, 13 (01) : 31 - 76
[2] Surface molecular characterisation of different epoxy resin composites subjected to UV accelerated degradation using XPS and ToF-SIMS
Awaja, Firas
Pigram, Paul J.
[J]. POLYMER DEGRADATION AND STABILITY, 2009, 94 (04) : 651 - 658
[3] Bociaga E., 2016, Przetworstwo Tworzyw, V22, P183
[4] UV-resistant GFRP composite using carbon nanotubes
Chennareddy, Rahulreddy
Tuwair, Hesham
Kandil, Usama F.
ElGawady, Mohamed
Taha, M. M. Reda
[J]. CONSTRUCTION AND BUILDING MATERIALS, 2019, 220 : 679 - 689
[5] Czub P., 2002, CHEMIA TECHNOLOGIA Z
[6] Impact of Application of Selected Composite Materials on the Weight and Vibroactivity of the Upper Gearbox Housing
Figlus, Tomasz
Koziol, Mateusz
Kuczynski, Lukasz
[J]. MATERIALS, 2019, 12 (16)
[7] Degradation of modified carbon black/epoxy nanocomposite coatings under ultraviolet exposure
Ghasemi-Kahrizsangi, Ahmad
Shariatpanahi, Homeira
Neshati, Jaber
Akbarinezhad, Esmaeil
[J]. APPLIED SURFACE SCIENCE, 2015, 353 : 530 - 539
[8] Improving the UV degradation resistance of epoxy coatings using modified carbon black nanoparticles
Ghasemi-Kahrizsangi, Ahmad
Neshati, Jaber
Shariatpanahi, Homeira
Akbarinezhad, Esmaeil
[J]. PROGRESS IN ORGANIC COATINGS, 2015, 85 : 199 - 207
[9] grandviewresearch, US
[10] Hinkley JA, 2012, LONG-TERM DURABILITY OF POLYMERIC MATRIX COMPOSITES, P1, DOI 10.1007/978-1-4419-9308-3_1

← 1 2 3 →