Study on microstructure and mechanical properties of spot welded joints of TRIP980 high strength steel

被引：0
|
作者：
Xie R. [1 ]
Li C. [1 ]
Zheng G. [1 ]
Chen F. [1 ]
机构：
[1] School of Materials Science and Engineering, Inner Mongolia University of Technology, Hohhot
来源：
Hanjie Xuebao/Transactions of the China Welding Institution | 2019年 / 40卷 / 01期
关键词：
Microstructure; Resistance spot welding; TRIP980 high strength steel;
D O I：
10.12073/j.hjxb.2019400024
中图分类号：
学科分类号：
摘要：
TRIP980 high strength steel was welded by resistance spot welding. By optimizing the parameters and process of resistance spot welding, the variation of microstructure and mechanical properties of weld nugget was studied. The results showed that the microstructure of nugget was gross martensite structure, the hardness of the joint was 617.1 HV and the maximum tensile force was 17.8 kN when optimized welding parameters were 9.5 kA, 22 cycle, 3 kN. Temper process was performed on the basis of this. When the tempering current and time were 6.3 kA and 13 cycles, respectively, the grain size of the joint microstructure was the smallest, the joint hardness reduced to 574.0 HV, and the joint tensile force was increased to 19.5 kN, increased by 9.6%. The fracture form was transformed from the original interface fracture to the button fracture. © 2019, Editorial Board of Transactions of the China Welding Institution, Magazine Agency Welding. All right reserved.
引用
收藏
页码：119 / 123and136
相关论文
共 11 条
  • [1] Li Y., Lou M., Lin Z., Light weighting of car body and its challenges to joining technologies, Journal of Mechanical Engineering, 48, 18, pp. 44-54, (2012)
  • [2] Zhang Y., Lai X., Zhu P., Et al., Lightweight design of automobile component using high strength steel based on dent resistance, Materials & Design, 27, 1, pp. 64-68, (2006)
  • [3] Wei S., Lu S., Effect of heat treatments on resistance spot weldability of TRIP 980 steel, Transactions of the China Welding Institution, 38, 8, pp. 115-118, (2017)
  • [4] Yang H., Zhang Y., Lai X., Et al., Critical specimen thickness of hot galvanized dual-phase steel spot welding, Transactions of the China Welding Institution, 29, 1, pp. 93-96, (2008)
  • [5] Yunbo X.U., Hou X., Wang Y., Et al., Effects of rapid heating continuous annealing on microstructure and mechanical properties of ultra high-strength TRIP-aided steel, Acta Metallurgica Sinica, 48, 2, pp. 176-182, (2012)
  • [6] Wang C., Ding H., Zhang J., Et al., Effect of partial replacement of Si with Al on the microstructures and mechanical properties of 1000 MPa TRIP steels, Journal of Materials Engineering & Performance, 23, 11, pp. 3896-3906, (2014)
  • [7] Sadasue T., Igi S., Taniguchi K., Et al., Fracture behaviour and numerical study of resistance spot welded joints in high-strength steel sheet, Welding International, 30, 8, pp. 602-613, (2016)
  • [8] Wei S.T., Liu R.D., Lu D., Et al., Study on fibre laser spot welding of TRIP980 steel, Materials Science & Technology, 31, 11, pp. 1271-1281, (2015)
  • [9] Mazzaferro C.C.P., Rosendo T.S., Tier M.A.D., Et al., Microstructural and mechanical observations of galvanized TRIP steel after friction stir spot welding, Advanced Manufacturing Processes, 30, 9, pp. 1090-1103, (2015)
  • [10] Cen Y., Chen F., Recent progress in numerical simulation of resistance seam welding, Transactions of the China Welding Institution, 37, 2, pp. 123-128, (2016)
12