FURTHER EXPLORATION ON CHARACTERISTIC REGION OF CRACK INITIATION FOR VERY-HIGH-CYCLE FATIGUE

被引:0
|
作者
Hong Y. [1 ]
机构
[1] LNM, Institute of Mechanics, Chinese Academy of Sciences, Beijing
来源
Lixue Xuebao/Chinese Journal of Theoretical and Applied Mechanics | 2022年 / 54卷 / 08期
关键词
characteristic region; crack initiation; high-strength steels; titanium alloys; very-high-cycle fatigue;
D O I
10.6052/0459-1879-22-276
中图分类号
学科分类号
摘要
With regard to very-high-cycle fatigue (VHCF) of high-strength metallic materials, we previously proposed the concept of crack initiation characteristic region and the related characteristic parameter (IJFatigue 2014, 58: 144-151), and proposed the numerous cyclic pressing (NCP) model to reveal the formation mechanism of this characteristic region (IJFatigue 2016, 89: 108-118). This crack initiation characteristic region is so-called fine granular area (FGA) on fracture surface for high-strength steels or rough area (RA) on fracture surface for titanium alloys. In recent years, the investigators in fatigue research field have paid great attention to the topic of crack initiation of VHCF for high-strength metallic materials and obtained new results. Therefore, several issues on this topic are of great interests and are necessary to be clearly addressed. These include: Does the microstructure refinement as well as nanograin formation in crack initiation characteristic region happen before or after crack initiation? What is the correlation between applied stress ratio and the formation of crack initiation characteristic region? What are the details of refined microstructure in crack initiation characteristic region including the thickness and the distribution of nanograins? Is vacuum environment the necessary condition for the formation of crack initiation characteristic region? What are the features of crack initiation characteristic region in different materials or with different loading modes? This article will clarify such issues by the comprehensive review of the recent results in the literature. This article will also briefly describe the important implications of the crack initiation characteristic region concept and the NCP model, which include: the assessment and prediction of VHCF properties for high-strength metallic materials, the approach to improve the VHCF properties of additively made metallic materials, and the possibility of manufacturing thin film metallic materials with nanograin microstructure. Specially, this article is dedicated to the memory of my supervisor Prof. Che-Min Cheng who passed away on August 25, 2021. © 2022 Chinese Journal of Theoretical and Applied Mechanics Press. All rights reserved.
引用
收藏
页码:2101 / 2118
页数:17
相关论文
共 41 条
  • [1] Hong Y, Lei Z, Sun C, Et al., Propensities of crack interior initiation and early growth for very-high-cycle fatigue of high strength steels, International Journal of Fatigue, 58, pp. 144-151, (2014)
  • [2] Zhao A, Xie J, Sun C, Et al., Prediction of threshold value for FGA formation, Materials Science & Engineering A, 528, pp. 6872-6877, (2011)
  • [3] Hong Y, Liu X, Lei Z, Et al., The formation mechanism of characteristic region at crack initiation for very-high-cycle fatigue of high-strength steels, International Journal of Fatigue, 89, pp. 108-118, (2016)
  • [4] Hong Y, Zhao A, Qian G, Et al., Fatigue strength and crack initiation mechanism of very-high-cycle fatigue for low alloy steels, Metallurgical and Materials Transactions A, 43, pp. 2753-2762, (2012)
  • [5] Sakai T, Takeda M, Shiozawa K, Et al., Experimental reconfirmation of characteristic S-N property for high carbon chromium bearing steel in wide life region in rotating bending, Journal of the Society of Materials Science, Japan, 49, 7, pp. 779-785, (2000)
  • [6] Murakami Yu, Nomoto T, Ueda T, Et al., On the mechanism of fatigue failure in the superlong life regime (N > 10<sup>7</sup> cycles), Part I: influence of hydrogen trapped by inclusions, Fatigue & Fracture of Engineering Materials & Structures, 23, pp. 893-902, (2000)
  • [7] Shiozawa K, Lu L, Ishihara S., S–N curve characteristics and subsurface crack initiation behaviour in ultra-long life fatigue of a high carbon –chromium bearing steel, Fatigue & Fracture of Engineering Materials & Structures, 24, pp. 781-790, (2001)
  • [8] Pan X, Hong Y., High-cycle and very-high-cycle fatigue behavior of a titanium alloy with equiaxed microstructure under different mean stresses, Fatigue & Fracture of Engineering Materials & Structures, 42, pp. 1950-1964, (2019)
  • [9] Liu X, Sun C, Hong Y., Effects of stress ratio on high-cycle and very-high-cycle fatigue behavior of a Ti–6Al–4V alloy, Materials Science & Engineering A, 622, pp. 228-235, (2015)
  • [10] Su H, Liu X, Sun C, Et al., Nanograin layer formation at crack initiation region for very-high-cycle fatigue of a Ti-6Al-4V alloy, Fatigue & Fracture of Engineering Materials & Structures, 40, pp. 979-993, (2017)