Pyrazolate-Bridged NHC Cyclometalated [Pt2] Complexes and [Pt2Ag(PPh3)]+ Clusters in Electroluminescent Devices

The ionic transition metal complexes (iTMCs) [{Pt((CC)-C-boolean AND*)(mu-Rpz)}(2)Ag(PPh3)]X ((HCC)-C-boolean AND* = 1-(4-(ethoxycarbonyl)phenyl)-3-methyl-1H-imidazole-2-ylidene, X = ClO4/PF6; Rpz = pz 1a/2a, 4-Mepz 1b/2b, and 3,5-dppz 1c/2c) were prepared from the neutral [{Pt((CC)-C-boolean AND*)(mu-Rpz)}(2)] (Rpz = pz A, 4-Mepz B, and 3,5-dppz C) and fully characterized. The "Ag(PPh3)" fragment is in between the two square-planar platinum units in an "open book" disposition and bonded through two Pt-Ag donor-acceptor bonds, as shown by X-ray diffraction (d(Pt-Ag) similar to 2.78 & Aring;, 1a-1c). Pt-195{H-1} and P-31{H-1} NMR confirmed that these solid-state structures remain in solution. Photoluminescence studies and theoretical calculations on 1a, were performed. The diphenylpyrazolate derivatives show the highest photoluminescence quantum yield (PLQY) in the solid state. Therefore, 2c and its neutral precursor C were selected as active materials on light-emitting devices. OLEDs fabricated with C showed a turn-on voltage of 3.2 V, a luminance peak of 21,357 cd m(-2) at 13 V, and a peak current efficiency of 28.8 cd A(-1) (9.5% EQE). They showed a lifetime t(50) of 15.7 h. OLEDs using 2c showed a maximum luminance of 114 cd m(-2), while LECs exhibited a maximum luminance of 20 cd m(-2) and a current efficiency of around 0.2 cd A(-1), with a t(50) value of 50 min.