Effect of nano-TiO2 size and utilization ratio on the performance of photocatalytic concretes; self-cleaning, fresh, and hardened state properties

被引：0
作者：
Şahin H.G. [1 ]
Temel M. [1 ]
Koçak G. [2 ]
Mardani A. [1 ]
Kara A. [2 ]
机构：
[1] Department of Civil Engineering, Bursa Uludag University, Bursa
[2] Department of Chemistry, Bursa Uludag University, Bursa
来源：
Environmental Science and Pollution Research | 2024年 / 31卷 / 25期
关键词：
Bohme abrasion resistance; Compressive-flexural strength; Dye removal; Nano-TiO[!sub]2[!/sub; Photocatalyst; Reactive Black 5;
D O I：
10.1007/s11356-024-33660-9
中图分类号：
学科分类号：
摘要：
In this study, photocatalysis technology was used to reduce water pollution. Decolorization of Reactive Black 5 using nano-TiO2 (NT) as a photocatalyst was investigated by adsorption and degradation experiments. Effects of NT particle size and utilization ratio on the time-dependent flow performance, compressive-flexural strength, and Bohme abrasion resistance of cementitious systems were investigated. In addition to the NT-free control mixture, a total of six photocatalytic self-cleaning mortar mixtures (PSCM) were prepared using NT in two different particle sizes (28 and 38 nm) and three different ratios (0.5%, 1%, and 1.5%). The PSCM sample containing 38 nm NT exhibited superior performance in terms of photocatalytic properties compared to the 28 nm state. It was observed that the flow performance of PSCM mixtures with NT substitution is adversely affected regardless of the NT type. Mixtures containing NT with a lower particle size (28 nm) had higher compressive and flexural strengths. © The Author(s) 2024.
引用
收藏
页码：37109 / 37124
页数：15
相关论文
共 108 条
[81]  
Salman M.M., Eweed K.M., Hameed A.M., Influence of partial replacement TiO2 nanoparticles on the compressive and flexural strength of ordinary cement mortar, Al-Nahrain J Eng Sci, 19, 2, pp. 265-270, (2016)
[82]  
Sanchez F., Sobolev K., Nanotechnology in concrete–a review, Constr Build Mater, 24, 11, pp. 2060-2071, (2010)
[83]  
Selvasofia S.A., Sarojini E., Moulica G., Thomas S., Tharani M., Saravanakumar P.T., Kumar P.M., Study on the mechanical properties of the nanoconcrete using nano-TiO2 and nanoclay, Mater Today: Proc, 50, pp. 1319-1325, (2022)
[84]  
Senff L., Hotza D., Lucas S., Ferreira V.M., Labrincha J.A., Effect of nano-SiO2 and nano-TiO2 addition on the rheological behavior and the hardened properties of cement mortars, Mater Sci Eng, A, 532, pp. 354-361, (2012)
[85]  
Sezer A., Mardani-Aghabaglou A., Boz A., Tanrinian N., An investigation into strength and permittivity of compacted sand-clay mixtures by partial replacement of water with lignosulfonate, Acta Physica Polonica, 130, pp. 23-27, (2016)
[86]  
Shanehsaz M., Seidi S., Ghorbani Y., Shoja S.M.R., Rouhani S., Polypyrrole-coated magnetic nanoparticles as an efficient adsorbent for RB19 synthetic textile dye: removal and kinetic study, Spectrochim Acta Part A Mol Biomol Spectrosc, 149, pp. 481-486, (2015)
[87]  
Sharma S., Kaur I., Gupta S., Effect of fly ash and nano titanium dioxide on compressive strength of concrete, Int Res J Eng Technol, 6, 7, pp. 2262-2265, (2019)
[88]  
Shen W., Zhang C., Li Q., Zhang W., Cao L., Ye J., Preparation of titanium dioxide nano particle modified photocatalytic self-cleaning concrete, J Clean Prod, 87, pp. 762-765, (2015)
[89]  
Singh L.P., Bhattacharyya S.K., Shah S.P., Mishra G., Ahalawat S., Sharma U., Studies on early stage hydration of tricalcium silicate incorporating silica nanoparticles: Part I, Constr Build Mater, 74, pp. 278-286, (2015)
[90]  
Slama H.B., Bouket A.C., Pourhassan Z., Alenezi F.N., Silini A., Cherif-Silini H., Oszako T., Luptakova T., Goli nska P., Diversity of synthetic dyes from textile ındustries, discharge ımpacts and treatment methods, Appl Sci, 11, 14, (2021)
234567891011