Effects of cold rolling and annealing time on fatigue resistance of AA5052 aluminum alloy

被引：0

作者：

Kusmono ^{[1
]}

Bora C. ^{[1
]}

Salim U.A. ^{[1
]}

机构：

[1] Department of Mechanical and Industrial Engineering, Faculty of Engineering, Universitas Gadjah Mada

来源：

International Journal of Engineering, Transactions B: Applications | 2021年 / 34卷 / 09期

关键词：

AA5052 aluminum alloy; Annealing; Cold rolling; Fatigue resistance;

D O I：

10.5829/IJE.2021.34.09C.16

中图分类号：

学科分类号：

摘要：

In the present study, the influences of cold rolling and annealing time on the fatigue crack propagation behavior of AA5052 aluminum alloy were investigated. The alloy sheet was cold-rolled under different rolling reductions, i.e., 0, 15, 30, and 45%. A 45% as-rolled specimen was then annealed at 370°C under different annealing times, i.e., for 2, 4, and 6 h. The microstructure evolutions after the cold rolling and annealing treatments were also examined using optical microscopy whereas the fatigue crack propagation behavior was characterized by using a fatigue test. Results showed that severely elongated grains were observed with increasing the rolling reduction. The elongated microstructures were changed into equaxial structures due to recrystallization during annealing treatment. The fatigue life was decreased drastically by increasing the rolling reduction but increased significantly with increasing annealing time. The fatigue life of the alloy was reduced by 93% when cold-rolled up to 45%. On the other hand, the fatigue life of the 45% rolled samples was increased significantly by 412% when annealed at 370ºC for 6 h. © 2021 Materials and Energy Research Center. All rights reserved.

引用

页码：2189 / 2197

页数：8

共 32 条

[1]

Xia S.L., Ma M., Zhang J.X., Wang W.X., Liu W.C., Effect of heating rate on the microstructure, texture and tensile properties of continuous cast AA5083 aluminum alloy, Materials Science and Engineering A, 609, pp. 168-176, (2014)

[2]

Panagopoulos C.N., Georgiou E.P., Cold rolling and lubricated wear of 5083 aluminium alloy, Materials and Design, 31, pp. 1050-1055, (2010)

[3]

Lin S., Nie Z., Huang H., Li B., Annealing behavior of a modified 5083 aluminum alloy, Materials and Design, 31, pp. 1607-1612, (2010)

[4]

Li M., Pan Q., Shi Y., Wang Y., Microstructure dependent fatigue crack growth in Al-Mg-Sc alloy, Materials Science & Engineering A, 611, pp. 142-151, (2014)

[5]

Liu J.T., Morris J., Recrystallization microstructures and textures in AA 5052 continuous cast and direct chill cast aluminum alloy, Materials Science and Engineering A, 385, pp. 342-351, (2004)

[6]

Daryadel M., Study on equal channel angular pressing process of AA7075 with copper casing by finite element-response Surface Couple Method, International Journal of Engineering: Transactions C: Aspects, 33, 12, pp. 2538-2548, (2020)

[7]

Morrisa D.G., Munoz-Morrisa M.A., Microstructure of severely deformed Al-3Mg and its evolution during annealing, Acta Materialia, 50, 16, pp. 4047-4060, (2002)

[8]

Tabatabaeia S.M.R., Zarasvand K.A., Investigating the effects of cold bulge forming speed on thickness variation and mechanical properties of aluminum alloys: Experimental and Numerical, International Journal of Engineering, Transaction C: Aspects, 31, 9, pp. 1602-1608, (2018)

[9]

Wang B., Chen X., Pan F., Mao J., Fang Y., Effects of cold rolling and heat treatment on microstructure and mechanical properties of AA 5052 aluminum alloy, Transaction Nonferrous Metal Society of China, 25, pp. 2481-2489, (2015)

[10]

Kusmono, Bora C., Salim U.A., Effects of cold rolling (CR) and annealing time on microstructure and mechanical properties of AA 5052 aluminum alloy, Metallurgy, 59, 4, pp. 485-488, (2020)

← 1 2 3 4 →