Investigating strengthening and softening mechanisms in Al/Ni multilayers via molecular dynamics simulations of uniaxial compression

被引:4
作者
Schwarz, Fabian [1 ]
Spolenak, Ralph [1 ]
机构
[1] Swiss Fed Inst Technol, Dept Mat, Lab Nanomet, Vladimir Prelog Weg 5, CH-8093 Zurich, Switzerland
关键词
SCALE-DEPENDENT DEFORMATION; DISLOCATION SOURCES; NANOINDENTATION; TENSION; INTERFACE; ALUMINUM; COATINGS; COPPER;
D O I
10.1063/5.0190198
中图分类号
O59 [应用物理学];
学科分类号
摘要
Due to their nanoscale features, nanometric multilayers can have a large variation in properties for varying bilayer heights. While the hardening at small feature sizes and the consequent softening at even smaller feature sizes have been observed for decades, the underlying mechanisms are still under debate. In this study, molecular dynamics uniaxial compression simulations are employed to study the mechanical properties of Al/Ni multilayers for bilayer heights h from 100 nm down to 5 nm. The effect of the microstructure on Young's modulus and the yield strength was investigated. Furthermore, the mechanical properties of equiatomic and equivolumetric multilayers were compared. A comparison with experimental results from the literature showed good agreement. Both the hardening at intermediate bilayer heights as well as the softening at very small bilayer heights were observed. The results are discussed in the context of possible hardening and softening mechanisms. While the Hall-Petch effect with a h(-1/2) scaling is not contradicted, it is shown that, although the underlying mechanisms are different, both the hardening as well as the softening are based on a general size effect with a scaling of ln(h)/h. (c) 2024 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).
引用
收藏
页数:8
相关论文
共 45 条
[1]   Multilayer coatings for improved performance [J].
Bull, SJ ;
Jones, AM .
SURFACE & COATINGS TECHNOLOGY, 1996, 78 (1-3) :173-184
[2]   What is behind the inverse Hall-Petch effect in nanocrystalline materials? [J].
Carlton, C. E. ;
Ferreira, P. J. .
ACTA MATERIALIA, 2007, 55 (11) :3749-3756
[3]   Molecular dynamics simulation of nanoindentation of nanocrystalline Al/Ni multilayers [J].
Chamani, M. ;
Farrahi, G. H. ;
Movahhedy, M. R. .
COMPUTATIONAL MATERIALS SCIENCE, 2016, 112 :175-184
[4]   Comparison of nanoindentation results obtained with Berkovich and cube-corner indenters [J].
Chudoba, T. ;
Schwaller, P. ;
Rabe, R. ;
Breguet, J. -M. ;
Michler, J. .
PHILOSOPHICAL MAGAZINE, 2006, 86 (33-35) :5265-5283
[5]   Interface structure and radiation damage resistance in Cu-Nb multilayer nanocomposites [J].
Demkowicz, M. J. ;
Hoagland, R. G. ;
Hirth, J. P. .
PHYSICAL REVIEW LETTERS, 2008, 100 (13)
[6]   The stress statistics of the first pop-in or discrete plastic event in crystal plasticity [J].
Derlet, P. M. ;
Maass, R. .
JOURNAL OF APPLIED PHYSICS, 2016, 120 (22)
[7]   Molecular dynamics simulations on nanoindentation mechanisms of multilayered films [J].
Fang, Te-Hua ;
Wu, Ha-Hung .
COMPUTATIONAL MATERIALS SCIENCE, 2008, 43 (04) :785-790
[8]   The mechanisms governing the activation of dislocation sources in aluminum at different strain rates [J].
Gurrutxaga-Lerma, B. ;
Balint, D. S. ;
Dini, D. ;
Sutton, A. P. .
JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 2015, 84 :273-292
[9]   THE DEFORMATION AND AGEING OF MILD STEEL .3. DISCUSSION OF RESULTS [J].
HALL, EO .
PROCEEDINGS OF THE PHYSICAL SOCIETY OF LONDON SECTION B, 1951, 64 (381) :747-753
[10]   Deformation and failure of shocked bulk Cu-Nb nanolaminates [J].
Han, W. Z. ;
Cerreta, E. K. ;
Mara, N. A. ;
Beyerlein, I. J. ;
Carpenter, J. S. ;
Zheng, S. J. ;
Trujillo, C. P. ;
Dickerson, P. O. ;
Misra, A. .
ACTA MATERIALIA, 2014, 63 :150-161