Structure,ElectricalConductingandThermalExpansionPropertiesofLn0.6Sr0.4Co0.8Fe0.2O3（Ln=La,Pr,Nd,Sm）Ceramics

被引：1

作者：

徐庆

机构：

[1] SchoolofMaterialsScienceandEngineering,WuhanUniversityofTechnology

来源：

JournalofWuhanUniversityofTechnology(MaterialsScienceEdition) | 2008年 / 03期

关键词：

electrical conduction; Perovskites; thermal expansion;

D O I：

暂无

中图分类号：

TB302 [工程材料试验];

学科分类号：

0805 ; 080502 ;

摘要：

Ln 0.6 Sr 0.4 Co 0.8 Fe 0.2 O 3 (Ln=La,Pr,Nd,Sm)perovskite-type complex oxides were synthesized using a glycine-nitrate process,and the structure,electrical conducting and thermal expansion properties of the resulting ceramics were examined with regard to the nature of the lanthanide cations.The results indicated that the La,Pr and Nd specimens had a rhombohedral symmetry,while an orthorhombic structure was determined for the Sm specimen.The pseudo-cubic lattice constant decreased with smaller lanthanide cations.It was found that the electrical conducting properties declined with decreasing lanthanide cation size.Fortunately, all the compositions remained rather high electrical conductivities exceeding 650Ω-1·cm-1 in the intermediate temperature range(600-800℃).An appreciable thermal expansion increase at high temperatures was detected for all the compositions.Decreasing the size of the lanthanide cations resulted in an increase of thermal expansion.With respect to the high electrical conductivities,the Ln 0.6 Sr 0.4 Co 0.8 Fe 0.2 O 3 oxides are considered to be acceptable as mixed conducting component in composite cathode designs together with doped ceria electrolytes.

引用

页码：386 / 390

页数：5

共 9 条

[1]

Oxygen transport in Ce 0.8 Gd 0.2 O 2? δ -based composite membranes[J] . V.V. Kharton,A.V. Kovalevsky,A.P. Viskup,A.L. Shaula,F.M. Figueiredo,E.N. Naumovich,F.M.B. Marques.Solid State Ionics . 2003 (3)

[2]

High temperature properties of La 0.6 Sr 0.4 Co 0.8 Fe 0.2 O 3? δ oxygen nonstoichiometry and chemical diffusion constant[J] . Masatoshi Katsuki,Shaorong Wang,Masayuki Dokiya,Takuya Hashimoto.Solid State Ionics . 2003 (3)

[3]

Crystal structure, thermal expansion and electrical conductivity of Nd 0.7 Sr 0.3 Fe 1? x Co x O 3 （0≤ x ≤0.8）[J] . Niladri Dasgupta,R Krishnamoorthy,K.Thomas Jacob.Materials Science ＆ Engineering B . 2002 (3)

[4]

Phase composition, oxidation state and electrical conductivity of SrFe 1.5? x Co x O y[J] . Zeng-qiang Deng,Guo-guang Zhang,Wei Liu,Ding-kun Peng,Chu-sheng Chen.Solid State Ionics . 2002

[5]

Performance of a La 0.6 Sr 0.4 Co 0.8 Fe 0.2 O 3 –Ce 0.8 Gd 0.2 O 1.9 –Ag cathode for ceria electrolyte SOFCs[J] . Shaorong Wang,Tohru Kato,Susumu Nagata,Takeo Honda,Toshimi Kaneko,Nobuharu Iwashita,Masayuki Dokiya.Solid State Ionics . 2002 (3)

[6]

Effect of the A Cation Size on the Structural, Magnetic, and Electrical Properties of Perovskites （La 1? x Nd x ） 0.7 Sr 0.3r003n MnO 3[J] . K Cherif,J Dhahri,E Dhahri,M Oumezzine,H Vincent.Journal of Solid State Chemistry . 2002 (2)

[7]

Optimisation of composite cathodes for intermediate temperature SOFC applications[J] . V. Dusastre,J.A. Kilner.Solid State Ionics . 1999 (1)

[8]

Properties of A-site-deficient La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3? δ -based perovskite oxides[J] . G.Ch Kostogloudis,Ch Ftikos.Solid State Ionics . 1999 (1)

[9]

Ln 0.4 Sr 0.6 Co 0.8 Fe 0.2 O 3? δ （Ln=La, Pr, Nd, Sm, Gd） for the electrode in solid oxide fuel cells[J] . H.Y Tu,Y Takeda,N Imanishi,O Yamamoto.Solid State Ionics . 1999 (3)

← 1 →