Formation and thermal stability of Cu-Zr-Al-Er bulk metallic glasses with high glass-forming ability

被引：2
|
作者：
Junying Fu Hua Men Shujie Pang Chaoli Ma and Tao Zhang Department of Materials Science and Engineering Behang University Beijing China [100083 ]
机构：
来源：
Journal of University of Science and Technology Beijing | 2007年 / S1期
关键词：
D O I：
暂无
中图分类号：
TG139.8 [];
学科分类号：
摘要：
The formation and thermal stabilities of Cu46.25Zr46.25xAl7.5Erx (x=0 to 8) bulk metallic glasses (BMGs) were investigated. The addition of a small amount of Er (2at%) for replacing Zr effectively improves the glass-forming ability of Cu46.25Zr46.25Al7.5 alloy, and the glassy rod with a diameter of at least 12 mm can be formed. The glass transition temperature (Tg), temperature interval of su- percooled liquid region △Tx (=Tx-Tg), and reduced glass transition temperature Trg (=Tg/Tl) of Cu46.25Zr44.25Al7.5Er2 glassy alloy are 699 K, 62 K and 0.607, respectively.
引用
收藏
页码：36 / 38
页数：3
相关论文
共 50 条
  • [1] Formation and thermal stability of Cu-Zr-AI-Er bulk metallic glasses with high glass-forming ability
    Fu, Junying
    Men, Hua
    Pang, Shujie
    Ma, Chaoli
    Zhang, Tao
    JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2007, 14 : 36 - 38
  • [2] Zr-Cu-Ni-Al bulk metallic glasses with superhigh glass-forming ability
    Sun, Y. J.
    Qu, D. D.
    Huang, Y. J.
    Liss, K. -D.
    Wei, X. S.
    Xing, D. W.
    Shen, J.
    ACTA MATERIALIA, 2009, 57 (04) : 1290 - 1299
  • [3] Formation and Thermal Stability of Cu-Based Metallic Glasses with High Glass-Forming Ability
    Zhou, B. W.
    Zhang, W.
    Zhang, X. G.
    Kimura, H.
    Makino, A.
    Inoue, A.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2012, 43A (08): : 2592 - 2597
  • [4] Formation and Thermal Stability of Cu-Based Metallic Glasses with High Glass-Forming Ability
    B. W. Zhou
    W. Zhang
    X. G. Zhang
    H. Kimura
    A. Makino
    A. Inoue
    Metallurgical and Materials Transactions A, 2012, 43 : 2592 - 2597
  • [5] Formation of Cu-Zr-Al-Er bulk metallic glass composites with enhanced deformability
    Song, K. K.
    Pauly, S.
    Sun, B. A.
    Zhang, Y.
    Tan, J.
    Kuehn, U.
    Stoica, M.
    Eckert, J.
    INTERMETALLICS, 2012, 30 : 132 - 138
  • [6] FORMATION OF La-Al-Ni-Cu-Fe BULK METALLIC GLASSES WITH HIGH GLASS-FORMING ABILITY
    Ji, Yunfei
    Pang, Shujie
    Ma, Chaoli
    Zhang, Tao
    INTERNATIONAL JOURNAL OF MODERN PHYSICS B, 2010, 24 (15-16): : 2314 - 2319
  • [7] Ni-free Zr-Fe-Al-Cu bulk metallic glasses with high glass-forming ability
    Zhang, Q. S.
    Zhang, W.
    Inoue, A.
    SCRIPTA MATERIALIA, 2009, 61 (03) : 241 - 244
  • [8] Effect of sulfur on the glass-forming ability, phase transformation, and thermal stability of Cu-Zr-Al bulk metallic glass
    Jiang, Hao-Ran
    Hu, Jing-Yi
    Neuber, Nico
    Bochtler, Benedikt
    Adam, Bastian
    Riegler, Sascha S.
    Frey, Maximilian
    Ruschel, Lucas
    Lu, Wen-Fei
    Feng, Ai-Han
    Busch, Ralf
    Shen, Jun
    ACTA MATERIALIA, 2021, 212
  • [9] Glass-forming ability and thermal stability of a new bulk metallic glass in the quaternary Zr-Cu-Ni-Al system
    Shen, J
    Zou, J
    Ye, L
    Lu, ZP
    Xing, DW
    Yan, M
    Sun, JF
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2005, 351 (30-32) : 2519 - 2523
  • [10] Zr-Co(Cu)-Al bulk metallic glasses with optimal glass-forming ability and their compressive properties
    Mohammadi Rahvard, Masoud
    Tamizifar, Morteza
    Boutorabi, Seyed Mohammad Ali
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2018, 28 (08) : 1543 - 1552
12345