Precipitation and heterogeneous strengthened CoCrNi-based medium entropy alloy with excellent strength-ductility combination from room to cryogenic temperatures

被引:0
|
作者
XIE Yu [1 ]
ZHAO PengCheng [1 ]
TONG YongGang [2 ]
TAN JianPing [1 ]
SUN BinHan [1 ]
CUI Yan [3 ]
WANG RunZi [1 ]
ZHANG XianCheng [1 ]
TU ShanTung [1 ]
机构
[1] Key Laboratory of Pressure Systems and Safety,Ministry of Education,School of Mechanical and Power Engineering,East China University of Science and Technology
[2] College of Automobile and Mechanical Engineering,Changsha University of Science and Technology
[3] Key Laboratory for Advanced Materials and Feringa Nobel Prize Scientist Joint Research Center,Institute of Fine Chemicals,School of Chemistry & Molecular Engineering,East China University of Science and
关键词
D O I
暂无
中图分类号
TG139 [其他特种性质合金];
学科分类号
摘要
The improved understandings of the mechanical properties as well as deformation mechanisms at cryogenic temperatures are the prerequisite for realizing the application of any new engineering materials to cryogenic industries. Here, a(CoCrNi)94Al3Ti3 medium entropy alloy(MEA) with nanoscale L12 coherent precipitates and heterogeneous grain structures was prepared by codoping Al and Ti elements with subsequent cold rolling and heat treatment processes. The mechanical properties were evaluated at the temperature range of 293–113 K. The ultimate strength of the MEA increases almost linearly from 1326 to 1695 MPa as the temperature decreases from 293 to 113 K, while the total elongation remains approximately constant of ~35%. The underlying deformation and strengthening mechanisms were investigated using various characterization techniques. Due to the effect of co-doped Al/Ti on channel width of the matrix and the increasing critical twinning stress induced by heterogeneous ultrafine grain size, the formation of deformation twins is inhibited at all temperatures. Consequently, only a slight increase of the deformation twins and stacking faults in the deformed specimens with a decreasing temperature, which leads to the relative temperature-independence of the ductility. The dislocation cutting mechanism of L12 coherent precipitates and the heterodeformation induced(HDI) hardening both significantly contribute to the strain hardening so that an excellent combination of strength and ductility is obtained. Additionally, the evolution of lattice friction stress with deformation temperature is determined by quantitative analysis, indicating an approximately linear relationship between the lattice friction and temperature. The present work provides new insights into the strategy of achieving outstanding strength-ductility synergy of the MEA under the wide temperature range by coupling heterogeneous ultrafine-grained structure and coherent precipitation strategy.
引用
收藏
页码:1780 / 1797
页数:18
相关论文
共 50 条
  • [1] Precipitation and heterogeneous strengthened CoCrNi-based medium entropy alloy with excellent strength-ductility combination from room to cryogenic temperatures
    XIE Yu
    ZHAO PengCheng
    TONG YongGang
    TAN JianPing
    SUN BinHan
    CUI Yan
    WANG RunZi
    ZHANG XianCheng
    TU ShanTung
    Science China(Technological Sciences), 2022, 65 (08) : 1780 - 1797
  • [2] Precipitation and heterogeneous strengthened CoCrNi-based medium entropy alloy with excellent strength-ductility combination from room to cryogenic temperatures
    Yu Xie
    PengCheng Zhao
    YongGang Tong
    JianPing Tan
    BinHan Sun
    Yan Cui
    RunZi Wang
    XianCheng Zhang
    ShanTung Tu
    Science China Technological Sciences, 2022, 65 : 1780 - 1797
  • [3] Precipitation and heterogeneous strengthened CoCrNi-based medium entropy alloy with excellent strength-ductility combination from room to cryogenic temperatures
    Xie Yu
    Zhao PengCheng
    Tong YongGang
    Tan JianPing
    Sun BinHan
    Cui Yan
    Wang RunZi
    Zhang XianCheng
    Tu ShanTung
    SCIENCE CHINA-TECHNOLOGICAL SCIENCES, 2022, 65 (08) : 1780 - 1797
  • [4] Hierarchical precipitates facilitate the excellent strength-ductility synergy in a CoCrNi-based medium-entropy alloy
    Wang, Qiang
    Zhang, Tuanwei
    Jiao, Zhiming
    Wang, Jianjun
    Zhao, Dan
    Wu, Guiying
    Qiao, Junwei
    Liaw, Peter K.
    Wang, Zhihua
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2023, 873
  • [5] Ta-doping induces heterogeneous microstructures in CoCrNi medium-entropy alloy to achieve excellent strength-ductility combination
    Xu, Dingfeng
    Wang, Xiaodi
    Yu, Fengshan
    Wang, Mingliang
    Lu, Yiping
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2023, 885
  • [6] Dual precipitates and heterogeneous fine-grain structure induced strength-ductility synergy in a CoCrNi-based medium-entropy alloy
    Chen, Yongan
    Li, Dazhao
    Xie, Ruofei
    Lu, Haitao
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2023, 867
  • [7] The bimodal nanocoherent precipitates leads to superior strength-ductility synergy in a novel CoCrNi-based medium entropy alloy
    Sun, K.
    Huang, P.
    Wang, F.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2022, 909
  • [8] Superior strength-ductility CoCrNi medium-entropy alloy wire
    Liu, Jun-Peng
    Chen, Jin-Xi
    Liu, Tian-Wei
    Li, Chen
    Chen, Yan
    Dai, Lan-Hong
    SCRIPTA MATERIALIA, 2020, 181 : 19 - 24
  • [9] Pursuing ultrahigh strength-ductility CoCrNi-based medium-entropy alloy by low-temperature pre-aging
    Li, A. X.
    Kang, K. W.
    Zhang, J. S.
    Xu, M. K.
    Huang, D.
    Liu, S. K.
    Jiang, Y. T.
    Li, G.
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2025, 220 : 115 - 128
  • [10] Superior strength-ductility synergy of an oxide-dispersion strengthened CoCrNi-based multi-principal element alloy
    Zhang, Yiqing
    Lu, Kaiju
    Jiang, Fengchun
    Chen, Yongxiong
    Liang, Xiubing
    MATERIALS RESEARCH LETTERS, 2024, 12 (11): : 825 - 833