ELECTRON-MICROSCOPY OF METASTABLE PHASES IN RAPIDLY SOLIDIFIED AL-CO ALLOYS

被引:7
|
作者
SURYANARAYANA, C
MENON, J
机构
[1] UNIV WINDSOR,DEPT MECH ENGN,ENGN MAT GRP,WINDSOR N9B 3P4,ONTARIO,CANADA
[2] BANARAS HINDU UNIV,DEPT MET ENGN,VARANASI 221005,UTTAR PRADESH,INDIA
关键词
AL-CO ALLOYS; TRANSMISSION ELECTRON MICROSCOPY; RAPID SOLIDIFICATION; SUPERSATURATED SOLID SOLUTIONS; METASTABLE INTERMEDIATE PHASES; DECAGONAL QUASI-CRYSTALLINE PHASE; POLYTYPISM; AMORPHOUS PHASE; TRANSFORMATION STUDIES;
D O I
10.1007/BF02747560
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Four binary AL-Co alloys containing 2.4, 14, 20 and 25 at.%Co and a ternary AL-Co-Si alloy with 20 at.% Co and 5 at.% Si were rapidly solidified from the liquid state by melt spinning. It has been shown that the solid solubility of Co in Al can be increased up to at least 1.7at.% from the negligible value under equilibrium conditions. Two metastable crystalline intermediate phases and a D1a-type ordered phase were observed in localized regions in the rapidly solidified Al-2-4at.%Co alloy. A quasicrystalline decagonal phase has been observed in all the other rapidly solidified alloys. This decagonal phase was shown to contain dislocations, dislocation loops and also twin-like defects. The phenomenon of polytypism was also observed in this decagonal quasicrystalline phase. In extremely thin areas of the Al-14at.%Co alloy ribbons on amorphous phase was detected. Transmission electron microscopy was used to extensively characterize the phases in the as-solidified condition and also those produced during and after transformation to the equilibrium constitution.
引用
收藏
页码:121 / 139
页数:19
相关论文
共 50 条
  • [32] ELECTRON-MICROSCOPY OF INERTIA FRICTION WELDMENTS IN A RAPIDLY SOLIDIFIED AL-FE-MO-V ALLOY
    HOU, KH
    BAESLACK, WA
    JOURNAL OF MATERIALS SCIENCE, 1990, 25 (05) : 2642 - 2653
  • [33] ANALYTICAL ELECTRON-MICROSCOPY OF PHASES IN AL-LI-CU-MG-ZR ALLOYS
    VECCHIO, KS
    WILLIAMS, DB
    JOURNAL OF METALS, 1987, 39 (07): : A30 - A30
  • [34] Undercooling and solidification behaviour of a metastable decagonal quasicrystalline phase and crystalline phases in Al-Co
    Schroers, J
    HollandMoritz, D
    Herlach, DM
    Grushko, B
    Urban, K
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 226 : 990 - 994
  • [35] METASTABLE PHASES IN RAPIDLY COOLED ALLOYS IN THE SYSTEM CO-P
    BASHEV, VF
    MIROSHNICHENKO, IS
    INORGANIC MATERIALS, 1983, 19 (06) : 775 - 777
  • [36] RAPIDLY SOLIDIFIED FE-NI-AL-C ALLOYS - METASTABLE PHASE FORMATION
    CHEN, HT
    MYERS, SA
    KOCH, CC
    MATERIALS SCIENCE AND ENGINEERING, 1988, 98 : 277 - 280
  • [37] COUPLED ZONE IN AL-CO ALLOYS
    BARCLAY, RS
    NIESSEN, P
    CANADIAN MINING AND METALLURGICAL BULLETIN, 1970, 63 (700): : 866 - &
  • [38] STUDY OF ALLOYS IN SYSTEM AL-CO
    PANTELEI.LA
    BADTIEV, EB
    ALESHINA, LV
    VESTNIK MOSKOVSKOGO UNIVERSITETA SERIYA 2 KHIMIYA, 1974, (01): : 117 - 118
  • [39] ANALYTICAL MICROSCOPY OF PRECIPITATES IN RAPIDLY SOLIDIFIED ALLOYS
    JACKSON, AG
    JOURNAL OF METALS, 1985, 37 (02): : 46 - 50
  • [40] Microstructural Investigations of Rapidly Solidified Al-Co-Y Alloys
    Avar, B.
    Gogebakan, M.
    Tarakci, M.
    Gencer, Y.
    Kerli, S.
    ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2013, 2013