MECHANICAL-PROPERTIES OF HIGH-STRENGTH LIGHTWEIGHT CONCRETE

被引：2

作者：

ZHANG, MH

GJORV, OE

机构：

来源：

ACI MATERIALS JOURNAL | 1991年 / 88卷 / 03期

关键词：

COMPRESSIVE STRENGTH; DENSITY (MASS VOLUME); HIGH-STRENGTH CONCRETES; LIGHTWEIGHT AGGREGATE CONCRETES; MECHANICAL PROPERTIES; MODULUS OF ELASTICITY; STRESS-STRAIN RELATIONSHIPS; TENSILE STRENGTH;

D O I：

暂无

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

Presents information on the mechanical properties of high-strength lightweight concrete up to 100 MPa with a corresponding density of 1865 kg/m3. Five different types of lightweight aggregates were investigated, and the strength of the aggregate appears to be the primary factor controlling the strength of the high-strength lightweight concrete. The tensile/compressive strength ratio appears to be lower for high-strength lightweight concrete than that for high-strength normal weight concrete, and the elastic modulus, which varied from 17.8 to 25.9 GPa, is much lower than that of normal weight concrete. The ultimate strain at peak load for the concrete varied from 3.3 to 4.6 mm/mm, which is higher than that of normal weight concrete. For the high-strength lightweight concrete, the shape of the ascending part of the stress-strain curve was more linear than that of lightweight concrete with low to medium strength.

引用

页码：240 / 247

页数：8

共 21 条

[1]

BURGE TA, 1983, SP79 AM CONCR I, P731

[2]

CARRASQUILLO RL, 1980, CEMENT CONCRETE AGGR, V2, P3

[3]

CARRASQUILLO RL, 1981, ACI J P, V78, P171

[4]

COOPER GA, 1972, J BRIT CERAMIC SOC, V71, P1

[5]

Hanson J.A., 1958, ACI J P, V55, P387

[6]

HOLM TA, 1980, APR P INT C LIGHTW C, P187

[7]

JOHSNTON CD, 1987, CEMENT CONCRETE AGGR, V9, P101

[8]

KAAR PH, 1978, SP55 AM CONCR I, P161

[9]

LYDON FD, 1980, J LIGHTWEIGHT CONCRE, V2, P125

[10]

MALHOTRA VM, 1987, JUN P UT HIGH STRENG, P15

← 1 2 3 →