THE EFFECT OF THERMAL ANNEALING ON THE ADHERENCE OF AL2O3-FILMS DEPOSITED BY LOW-PRESSURE, METAL-ORGANIC, CHEMICAL-VAPOR-DEPOSITION ON AISI-304

被引：6
作者：
HAANAPPEL, VAC
VANDERVENDEL, D
VANCORBACH, HD
FRANSEN, T
GELLINGS, PJ
机构：
[1] Department of Chemical Technology, University of Twente, Enschede
来源：
OXIDATION OF METALS | 1995年 / 43卷 / 5-6期
关键词：
METAL-ORGANIC; CHEMICAL-VAPOR DEPOSITION (MOCVD); THERMAL ANNEALING; ALUMINA FILMS; SCANNING SCRATCH TEST (SST); ADHERENCE;
D O I：
10.1007/BF01046893
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Thin alumina films, deposited at 280 degrees C by low-pressure, metal-organic, chemical-vapor deposition on stainless steel, type AISI 304, were annealed at 0.17 kPa in a nitrogen atmosphere for 2, 4, and 17 hr at 600, 700, and 800 degrees C. The effect of the annealing process on the adhesion of the thin alumina films was studied using a scanning-scratch tester, type SST-101, developed by Shimadzu. The best mechanical properties were obtained with unannealed samples. After thermal annealing the critical load decreased proportional to annealing time and/or temperature. This effect was probably due to the presence of a high thermal stress and to preferential segregation of sulfur near the oxide-alloy interface.
引用
收藏
页码：459 / 478
页数：20
相关论文
共 26 条
[1]   SURFACE SEGREGATION IN AUSTENITIC STAINLESS-STEEL [J].
BRIANT, CL ;
MULFORD, RA .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1982, 13 (05) :745-752
[2]  
DESU SB, 1990, MATER RES SOC SYMP P, V168, P221
[3]   REACTIVE ELEMENT - SULFUR INTERACTION AND OXIDE SCALE ADHERENCE [J].
FUNKENBUSCH, AW ;
SMEGGIL, JG ;
BORNSTEIN, NS .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (06) :1164-1166
[4]  
FUNKENBUSCH AW, 1983, P8319 OFF NAV RES TE
[5]   CRACKING AND DELAMINATION OF METAL-ORGANIC VAPOR-DEPOSITED ALUMINA AND SILICA FILMS [J].
HAANAPPEL, VAC ;
VANCORBACH, HD ;
FRANSEN, T ;
GELLINGS, PJ .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1993, 167 (1-2) :179-185
[6]  
HAANAPPEL VAC, IN PRESS SURF COAT T
[7]  
HAANAPPEL VAC, 1994, THESIS U TWENTE NETH
[8]   MICROSTRUCTURE, ADHESION AND GROWTH-KINETICS OF PROTECTIVE SCALES ON METALS AND ALLOYS [J].
HINDAM, H ;
WHITTLE, DP .
OXIDATION OF METALS, 1982, 18 (5-6) :245-284
[9]  
Hocking M. G., 1989, METALLIC CERAMIC COA
[10]  
HOFMAN R, 1993, THESIS U TWENTE NETH
123