Pulsed current and dual pulse gas metal arc welding of grade AISI: 310S austenitic stainless steel

The transverse shrinkage, mechanical and metallurgical properties of AISI: 310S ASS weld joints prepared by P-GMAW and DP-GMAW processes were investigated. It was observed that the use of the DP-GMAW process improves the aforementioned characteristics in comparison to that of the P-GMAW process. The enhanced quality of weld joints obtained with DP-GMAW process is primarily due to the combined effect of pulsed current and thermal pulsation (low frequency pulse). During the thermal pulsation period, there is a fluctuation of wire feed rate, which results in the further increase in welding current and the decrease in arc voltage. Because of this synchronization between welding current and arc voltage during the period of low frequency pulse, the DP-GMAW deposit introduces comparatively more thermal shock compared to the P-GMAW deposit, thereby reducing the heat input and improves the properties of weld joints. Copyright (C) 2015, China Ordnance Society. Production and hosting by Elsevier B.V. All rights reserved.