INITIAL PRECIPITATION BEHAVIOR OF ALUMINUM HYDROXIDE PARTICLES FROM ALUMINUM SALT SOLUTION IN THE PRESENCE OF SULFATE ION

被引：0
作者：
YADA, M
NAGAI, H
KATO, A
机构：
[1] Department of Chemical Science and Technology, Faculty of Engineering, Kyushu University, Hakozaki, Higashi-ku
来源：
NIPPON KAGAKU KAISHI | 1993年 / 09期
关键词：
D O I：
10.1246/nikkashi.1993.1091
中图分类号：
O6 [化学];
学科分类号：
0703 ;
摘要：
On the synthesis of aluminum hydroxide from aluminum salt solution by homogeneous precipitation method using urea, the initial prcipitation behavior of aluminum hydroxide in the presence of sulfate ion was investigated. It was observed that the growth of aluminum hydroxide particles occurred discretely up to ca. 80 nm in diameter, but above this size the growth occurred by accompanying the particle coalescence in the course of the precipitation of aluminum hydroxide. This agrees with the previous observation.
引用
收藏
页码：1091 / 1095
页数：5
相关论文
共 7 条
[1]  
BLENDELL JE, 1984, AM CERAM SOC BULL, V63, P797
[2]   ALUMINUM HYDROUS OXIDE SOLS .1. SPHERICAL-PARTICLES OF NARROW SIZE DISTRIBUTION [J].
BRACE, R ;
MATIJEVI.E .
JOURNAL OF INORGANIC & NUCLEAR CHEMISTRY, 1973, 35 (11) :3691-3705
[3]   ALUMINUM HYDROUS OXIDE SOLS .2. PREPARATION OF UNIFORM SPHERICAL-PARTICLES BY HYDROLYSIS OF AL SEC-BUTOXIDE [J].
CATONE, DL ;
MATIJEVIC, E .
JOURNAL OF COLLOID AND INTERFACE SCIENCE, 1974, 48 (02) :291-301
[4]  
DEHEK H, 1978, J COLLOID INTERF SCI, V61, P72
[5]  
NAGAI H, 1991, BRIT CERAM TRANS J, V90, P44
[6]  
SACKS MD, 1984, AM CERAM SOC BULL, V63, P301
[7]  
Willard HH, 1937, J AM CHEM SOC, V59, P1190, DOI 10.1021/ja01286a010
1