THE EFFECT OF AGING ON WEAR CHARACTERISTICS OF RHEOCAST-LEADED ALUMINUM-ALLOYS

被引:24
作者
SRIVASTAVA, SK
MOHAN, S
AGARWALA, V
AGARWALA, RC
机构
[1] BHU IT,DEPT MET ENGN,VARANASI,UTTAR PRADESH,INDIA
[2] UNIV ROORKEE,DEPT MET ENGN,ROORKEE 247667,UTTAR PRADESH,INDIA
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1994年 / 25卷 / 04期
关键词
D O I
10.1007/BF02665461
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In the last few decades, much work has been carried out on leaded aluminum alloys in as-cast condition, but recently, an attempt was made to study the effect of aging on the wear behavior of leaded aluminum alloys. The unique behavior of wear is very similar to the hardness behavior with the aging of partially homogenized Al-Cu alloys investigated earlier. A minimum in bulk wear was observed at about 2 hours of aging. The maximum and minimum in bulk wear are observed to decrease with an increase in sliding velocity. It was also observed that the maximum in bulk wear is attained at lower aging periods.
引用
收藏
页码:851 / 856
页数:6
相关论文
共 22 条
  • [1] AGARWALA V, 1987, Z METALLKD, V78, P506
  • [2] AGARWALA V, 1986, Z METALLKD, V77, P815
  • [3] AGARWALA V, 1990, INT C RECRYSTALLIZAT, P843
  • [4] AVRAAMOV YS, 1985, MAT SCI HEAT TREAT, V26, P543
  • [5] Borgunov V. C., 1973, RUSS CAST PROD, V9, P353
  • [6] DOBATKIN VI, 1979, IZV AKAD NAUK SSSR, V1, P105
  • [7] GARG R, 1993, Z METALLKD, V84, P721
  • [8] ICHIKAWA K, 1987, T JPN I MET, V228, P145
  • [9] MICROSTRUCTURE AND SUPERCONDUCTING PROPERTIES OF MELT-QUENCHED INSOLUBLE AL-PB AND AL-PB-BI ALLOYS
    INOUE, A
    YANO, N
    MATSUZAKI, K
    MASUMOTO, T
    [J]. JOURNAL OF MATERIALS SCIENCE, 1987, 22 (01) : 123 - 131
  • [10] MACKAY ML, 1977, MET PROG, V111, P32