EFFECT OF HEAT-TREATMENT AND DEVIATION FROM STOICHIOMETRY ON THE STRUCTURE AND PHYSICAL-PROPERTIES OF TITANIUM NICKELIDE

被引：0
作者：
BELOUSOV, OK
机构：
来源：
METAL SCIENCE AND HEAT TREATMENT | 1979年 / 21卷 / 7-8期
关键词：
D O I：
10.1007/BF00703670
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
1. Alloys containing 48-50 at. % Ni are not hardened from 980°, while β phase is formed after quenching of alloys with >50.8% Ni. 2. The properties of quenched alloys do not change as the result of holding at room temperature for as long as 5500 h. 3. Prolonged annealing at 500-450° leads to formation of finely dispersed phase and lower electrical resistivity of alloys with 50.2-51.8 at. % Ni. Alloys with 49.8-50.2 at. % Ni are insensitive to all the heat treatments tested. © 1980 Plenum Publishing Corporation.
引用
收藏
页码：557 / 560
页数：4
相关论文
共 4 条
[1]  
HANLON JE, 1967, T METALL SOC AIME, V239, P1323
[2]  
Kornilov I. I., 1971, Fizika Metallov i Metallovedenie, V32, P420
[3]  
TOSHIO H, 1975, J JAP I METALS, V39, P175
[4]   HOMOGENEITY RANGE AND MARTENSITIC TRANSFORMATION IN TINI [J].
WASILEWSKI, RJ ;
BUTLER, SR ;
HANLON, JE ;
WORDEN, D .
METALLURGICAL TRANSACTIONS, 1971, 2 (01) :229-+
1