HIGH-PERFORMANCE GEL-PERMEATION CHROMATOGRAPHY OF POLYSTYRENE

Microparticulate crosslinked polystyrene packings in short columns have been investigated with high performance liquid chromatography instrumentation. Reliable molecular weight data for six polystyrene standards having narrow molecular weight distributions and for a polystyrene having a broad distribution have been obtained by optimizing the injection procedure, using a constant flow pump, and incorporating an internal standard into each injected solution. Experimental determinations of the dependence of the polydispersity for polystyrene standards on eluent flow rate and polymer diffusion coefficient were in agreement with a relation predicted from theoretical considerations of chromotogram broadening. Because of the dependence of chromatogram broadening on polystyrene molecular weight, high efficiency separations for high polymers were only obtained at low eluent flow rates. For low polymers, high efficiency separations may be performed at fast eluent flow rates. It was concluded that accurate molecular weight distributions can only be determined from chromatograms obtained at low eluent flow rates, which was supported by experimental measurements of polydispersity on polystyrene sample prepared by a radical polymerization at low monomer conversion. A differential weight distribution calculated from an experimental chromatogram for the polydisperse polystyrene determined at the lowest eluent flow rate (0.1 cm3min-1) was compared with distributions predicted theoretically for polystyrenes prepared by radical polymerization. It was concluded that the experimental distribution contained a small contribution from chromatogram broadening and that most of the radicals in the polymerization of styrene terminated by combination. © 1979.