High-Temperature Corrosion of T92 Steel in N-2/H2O/H2S-Mixed Gas

被引：3

作者：

Shi, Yuke ^{[1
]}

Kim, Min Jung ^{[1
]}

Park, Soon Yong ^{[1
]}

Abro, M. Ali ^{[1
]}

Yadav, Poonam ^{[1
]}

Lee, Dong Bok ^{[1
]}

机构：

[1] Sungkyunkwan Univ, Sch Adv Mat Sci & Engn, Suwon 16419, South Korea

来源：

CORROSION SCIENCE AND TECHNOLOGY-KOREA | 2016年 / 15卷 / 03期

关键词：

Fe-Cr alloys; corrosion; sulfidation; H2S;

D O I：

10.14773/cst.2016.15.3.125

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

The ASTM T92 steel was corroded at 600 degrees C and 800 degrees C at 1 atm of N-2/3.1% H2O/2.42% H2S-mixed gas. The formed scales were thick and fragile. They consisted primarily of the outer FeS scale and the inner (FeS, FeCr2S4)-mixed scale containing a small amount of the Cr2O3 scale. This indicated that corrosion occurred mainly via sulfidation rather than oxidation due to the H2S gas. Since FeS was present throughout the whole scale, T92 steel was non-protective, displaying high corrosion rates.

引用

页码：125 / 128

页数：4

共 7 条

[1] SULFIDATION OF IRON AT HIGH-TEMPERATURES AND DIFFUSION KINETICS IN FERROUS SULFIDE
DANIELEWSKI, M
MROWEC, S
STOKLOSA, A
[J]. OXIDATION OF METALS, 1982, 17 (1-2): : 77 - 97
[2] Lee H. J., 2014, CORROS SCI TECH, V13, P2
[3] TRANSPORT-PROPERTIES OF SULFIDE SCALES AND SULFIDATION OF METALS AND ALLOYS
MROWEC, S
PRZYBYLSKI, K
[J]. OXIDATION OF METALS, 1985, 23 (3-4): : 107 - 139
[4] KINETICS AND MECHANISM OF HIGH-TEMPERATURE SULFUR CORROSION OF FE-CR-AL ALLOYS
MROWEC, S
WEDRYCHOWSKA, M
[J]. OXIDATION OF METALS, 1979, 13 (06): : 481 - 504
[5] Mrowec S., 1969, OXID MET, V1, P1
[6] Nguyen T. D., 2015, CORROS SCI TECH, V14, P3
[7] The sulfidation behavior of several commercial ferritic and austenitic steels
Schulte, M
Rahmel, A
Schutze, M
[J]. OXIDATION OF METALS, 1998, 49 (1-2): : 33 - 70

← 1 →