Influence of electron-beam parameters on the radiation-induced formation of graphitic onions

被引：46

作者：

Lulli, G

Parisini, A

Mattei, G

机构：

[1] Istituto LAMEL-CNR, I-40129 Bologna

来源：

ULTRAMICROSCOPY | 1995年 / 60卷 / 02期

关键词：

D O I：

10.1016/0304-3991(95)00074-X

中图分类号：

TH742 [显微镜];

学科分类号：

摘要：

It is shown that to form spherical graphitic onions by intense electron bombardment of graphitized carbon inside the electron microscope, irradiation must be performed at energies above the threshold of elastic atomic displacement, and at beam current densities higher than about 150 A cm(-2). Under these strong non-equilibrium conditions, it is possible to obtain the dynamic stability of the spherical shells, which appear fundamentally unstable in absence of irradiation.

引用

收藏

页码：187 / 194

页数：8

相关论文

共 13 条

[1] STRUCTURAL DEFECTS AND THE SHAPE OF LARGE FULLERENES [J].

BRABEC, CJ ;

MAITI, A ;

BERNHOLC, J .

CHEMICAL PHYSICS LETTERS, 1994, 219 (5-6) :473-478

[2]

CORBETT JW, 1975, POINT DEFECTS SOLIDS, V2, P399

[3] CARBON ONIONS PRODUCED BY HEAT-TREATMENT OF CARBON SOOT AND THEIR RELATION TO THE 217.5 NM INTERSTELLAR ABSORPTION FEATURE [J].

DEHEER, WA ;

UGARTE, D .

CHEMICAL PHYSICS LETTERS, 1993, 207 (4-6) :480-486

[4] DIRECT OBSERVATION OF THE TETRAHEDRAL BONDING IN GRAPHITIZED CARBON-BLACK BY HIGH-RESOLUTION ELECTRON-MICROSCOPY [J].

IIJIMA, S .

JOURNAL OF CRYSTAL GROWTH, 1980, 50 (03) :675-683

[5]

IJIMA S, 1991, NATURE, V354, P56

[6] C-60 - BUCKMINSTERFULLERENE [J].

KROTO, HW ;

HEATH, JR ;

OBRIEN, SC ;

CURL, RF ;

SMALLEY, RE .

NATURE, 1985, 318 (6042) :162-163

[7]

KROTO HW, 1992, J CHEM SOC DA, V20, P2141

[8] SOLID-PHASE EPITAXY OF AMORPHOUS-SILICON INDUCED BY ELECTRON-IRRADIATION AT ROOM-TEMPERATURE [J].

LULLI, G ;

MERLI, PG ;

ANTISARI, MV .

PHYSICAL REVIEW B, 1987, 36 (15) :8038-8042

[9] STRUCTURE AND ENERGETICS OF SINGLE AND MULTILAYER FULLERENE CAGES [J].

MAITI, A ;

BRABEC, CJ ;

BERNHOLC, J .

PHYSICAL REVIEW LETTERS, 1993, 70 (20) :3023-3026

[10] NEAR-THRESHOLD ION-INDUCED DEFECT PRODUCTION IN GRAPHITE [J].

MARTON, D ;

BOYD, KJ ;

LYTLE, T ;

RABALAIS, JW .

PHYSICAL REVIEW B, 1993, 48 (10) :6757-6766