SPACE-GROUP DETERMINATION AND STRUCTURE MODEL FOR KAPPA-AL2O3 BY CONVERGENT-BEAM ELECTRON-DIFFRACTION (CBED)

被引:78
作者
LIU, P [1 ]
SKOGSMO, J [1 ]
机构
[1] CHALMERS UNIV TECHNOL,DEPT PHYS,S-41296 GOTHENBURG,SWEDEN
来源
ACTA CRYSTALLOGRAPHICA SECTION B-STRUCTURAL SCIENCE | 1991年 / 47卷
关键词
D O I
10.1107/S010876819100071X
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
The crystal structure of kappa-Al2O3, which was produced by chemical vapour deposition, has been examined by convergent-beam electron diffraction combined with selected-area electron diffraction and high-resolution electron microscopy. The crystal structure of kappa-Al2O3 has been found to be orthorhombic, space group Pna2(1). The lattice parameters are a = 4.69, b = 8.18 and c = 8.87 angstrom. The volume is 340.3 angstrom 3 and the density is approximately 3.98 g cm-3, Z = 8. Three different variants of kappa-Al2O3 domains give rise to a false superlattice which can be described by a hexagonal structure. An atomic model for kappa-Al2O3 based on the experimental results has been constructed.
引用
收藏
页码:425 / 433
页数:9
相关论文
共 25 条
[11]  
RICHERSON DW, 1982, MODERN CERAMIC ENG, P9
[12]  
Saalfeld H., 1960, N JAHRB MINERAL ABH, V95, P1
[13]  
SKOGSMO J, 1989, THESIS CHALMERS U TE
[14]  
SKOGSMO J, 1984, J PHYS-PARIS, V9, P447
[15]  
SKOGSMO J, 1989, 12TH P INT PLANS SEM, V3, P129
[16]  
SKOGSMO J, 1985, 5TH P EUR C CVD SWED, P364
[17]  
Steeds J.W., 1979, INTRO ANAL ELECTRON, P387, DOI [10.1007/978-1-4757-5581-7, 10.1007/978-1-4757-5581-7_15]
[18]   USE OF HIGH-SYMMETRY ZONE AXES IN ELECTRON-DIFFRACTION IN DETERMINING CRYSTAL POINT AND SPACE-GROUPS [J].
STEEDS, JW ;
VINCENT, R .
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1983, 16 (JUN) :317-324
[19]  
TANAKA M, 1985, CONVERGENT BEAM ELEC, P160
[20]  
TANAKA M, 1982, 10TH P INT C EL MICR, V1, P631