EFFECT OF PLASTIC STRAIN INCOMPATIBILITY ON 0.1-PERCENT PROOF STRESSES OF ZINC BICRYSTALS

被引:10
作者
MARUYAMA, K
AKABORI, M
KARASHIMA, S
机构
来源
TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS | 1981年 / 22卷 / 10期
关键词
ZINC METALLOGRAPHY - Microstructures;
D O I
10.2320/matertrans1960.22.723
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Deformation behavior of three kinds of isoaxial zinc bicrystals is described to clarify the effects of grain boundaries on plastic deformation. The increase in 0. 1% proof stress is caused by multiple slips near a grain boundary which is induced to release incompatibility.
引用
收藏
页码:723 / 732
页数:10
相关论文
共 32 条
[1]   DEFORMATION OF PLASTICALLY NON-HOMOGENEOUS MATERIALS [J].
ASHBY, MF .
PHILOSOPHICAL MAGAZINE, 1970, 21 (170) :399-&
[2]   EFFECT OF ORIENTATION DIFFERENCE ON THE PLASTIC DEFORMATION OF ALUMINUM BICRYSTALS [J].
AUST, KT ;
CHEN, NK .
ACTA METALLURGICA, 1954, 2 (04) :632-&
[3]   BETA-BRASS BICRYSTAL STRESS-STRAIN RELATIONS [J].
CHUANG, YD ;
MARGOLIN, H .
METALLURGICAL TRANSACTIONS, 1973, 4 (08) :1905-1917
[4]  
CHUNG IS, 1981, THESIS TOHOKU U
[5]   NUCLEATION OF DEFORMATION TWINS IN ZINC BICRYSTALS [J].
CHYUNG, CK ;
WEI, CT .
PHILOSOPHICAL MAGAZINE, 1967, 15 (133) :161-&
[6]   MECHANICAL DEFORMATION OF ALUMINIUM BICRYSTALS [J].
CLARK, R ;
CHALMERS, B .
ACTA METALLURGICA, 1954, 2 (01) :80-86
[7]   SLIP BAND CONTINUITY ACROSS GRAIN BOUNDARIES IN ALUMINUM [J].
DAVIS, KG ;
TEGHTSOO.E ;
LU, A .
ACTA METALLURGICA, 1966, 14 (12) :1677-&
[8]   DEFORMATION AND FRACTURE OF ALPHA-BETA-BRASS 2-PHASE BICRYSTALS AT 150-K [J].
FATHALLA, N ;
TAKASUGI, T ;
IZUMI, O .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (09) :1341-1349
[9]   OPERATIVE SLIP SYSTEMS IN ALPHA-BETA BRASS 2-PHASE BICRYSTALS AT 150-K [J].
FATHALLA, N ;
TAKASUGI, T ;
IZUMI, O .
JOURNAL OF MATERIALS SCIENCE, 1979, 14 (07) :1651-1656
[10]   DEFORMATION OF ALUMINUM BICRYSTALS WITH A COMPOSITE CRYSTAL ORIENTED FOR A SCHMID FACTOR OF 0.5 IN LOW STRAIN RANGE LESS THAN 10-3 [J].
FUJITA, H ;
TOYODA, K ;
KANETSUKI, Y .
TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1975, 16 (03) :151-162