CARBIDE-DISPERSION-STRENGTHENED B2 NIAL

被引:27
作者
JHA, SC
RAY, R
WHITTENBERGER, JD
机构
[1] NASA,LEWIS RES CTR,CLEVELAND,OH 44135
[2] MARKO MAT INC,N BILLERICA,MA 01862
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1989年 / 119卷 / 1-2期
关键词
Carbides; -; Metallography--Precipitation;
D O I
10.1016/0921-5093(89)90529-7
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The microstructure and high temperature deformation behavior of a rapidly solidified and hot-extruded NiAl-4%HfC alloy are described. Rapid solidification processing led to the incorporation of 20-50 nm sized HfC precipitates in a B2-ordered NiAl matrix. The carbide precipitates were found to be stable and resistant to coarsening at temperatures as high as 1500 K. The as-extruded microstructure consisted of a recrystallized grain structure, with grain size in the range 5-8 μm. Transmission electron microscopy on the as-extruded alloy revealed the presence of subgrains, and a dislocation substructure stabilized by the carbide precipitates. Departure side pinning of matrix dislocations at the carbide precipitates was observed in the as-extruded material. The flow characteristics of NiAl-4%HfC alloy were investigated by constant-velocity compression testing at 1200 and 1300 K, with strain rates ranging from 10-4 to 10-7 s-1. It was observed that carbide-containing NiAl continuously work hardened at all temperatures and strain rates investigated. The flow stress-strain rate data indicated the presence of a threshold stress for the creep deformation of carbide-dispersion-strengthened NiAl intermetallic, and departure side pinning of dislocations by the carbide precipitates was also observed in the deformed sample.
引用
收藏
页码:103 / 111
页数:9
相关论文
共 25 条
[1]   THE STRUCTURE OF EXTRUDED NIAL [J].
BAKER, I ;
SCHULSON, EM .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1984, 15 (06) :1129-1136
[2]   EFFECT OF 0.1 AT-PERCENT ZIRCONIUM ON THE CYCLIC OXIDATION RESISTANCE OF BETA-NIAL [J].
BARRETT, CA .
OXIDATION OF METALS, 1988, 30 (5-6) :361-390
[3]   PLASTIC-DEFORMATION OF NIAL SINGLE-CRYSTALS BETWEEN 300 DEGREES 5 AND 1050 DEGREES K .1. EXPERIMENTAL EVIDENCE ON ROLE OF KINKING AND UNIFORM DEFORMATION IN CRYSTALS COMPRESSED ALONG [001] [J].
FRASER, HL ;
SMALLMAN, RE ;
LORETTO, MH .
PHILOSOPHICAL MAGAZINE, 1973, 28 (03) :651-665
[4]   DUCTILITY IN RAPIDLY SOLIDIFIED NIAL [J].
GAYDOSH, DJ ;
JECH, RW ;
TITRAN, RH .
JOURNAL OF MATERIALS SCIENCE LETTERS, 1985, 4 (02) :138-140
[5]  
GRALA EM, 1960, MECHANICAL PROPERTIE, P358
[6]   ROOM-TEMPERATURE TENSILE DUCTILITY IN POLYCRYSTALLINE B2 NIAL [J].
HAHN, KH ;
VEDULA, K .
SCRIPTA METALLURGICA, 1989, 23 (01) :7-12
[7]   DISPERSOIDS IN RAPIDLY SOLIDIFIED B2 NICKEL ALUMINIDES [J].
JHA, SC ;
RAY, R ;
GAYDOSH, DJ .
SCRIPTA METALLURGICA, 1989, 23 (05) :805-810
[8]   DISPERSION STRENGTHENED NIAL ALLOYS PRODUCED BY RAPID SOLIDIFICATION PROCESSING [J].
JHA, SC ;
RAY, R .
JOURNAL OF MATERIALS SCIENCE LETTERS, 1988, 7 (03) :285-288
[9]   THE THRESHOLD STRESS AND DEPARTURE SIDE PINNING OF DISLOCATIONS BY DISPERSOIDS [J].
NARDONE, VC ;
MATEJCZYK, DE ;
TIEN, JK .
ACTA METALLURGICA, 1984, 32 (09) :1509-1517
[10]  
PATHARE VM, 1985, MODERN DEV POWDER ME, V16, P695