STATICS AND DYNAMICS OF OMEGA-FUNCTIONALIZED BLOCK-COPOLYMERS OF STYRENE AND ISOPRENE

The statics and dynamics of omega-functionalized diblock copolymers of styrene and isoprene have been studied with small-angle X-ray scattering(SAXS) and with theology and dielectric spectroscopy. The asymmetric diblock copolymers (w(PS) approximate to 30%) had a dimethylamino or zwitterion group at either end of the chain, and the molecular weights were in the range (0.62-2.44) x 10(4). Depending on the temperature, the SAXS results revealed two separate levels of microphase separation, one between the polystyrene (PS) and polyisoprene (PI) blocks forming the microdomain structure and another one between ionic and nonionic material. The latter process creates sufficient contrast notwithstanding the small fraction of the zwitterionic groups. When the zwitterion is linked to the PI chain end, aggregates are formed at low temperatures within the PI phase. These aggregates manifest themselves both in theology and in dielectric spectroscopy, respectively, with an extended rubbery plateau and with a new dielectric process associated with restricted PI segmental relaxation. When the zwitterion is located on the PS chain end, association takes place, at high temperatures, within the PS phase and acts to stabilize the new microdomain up to very high temperatures. When compared with neutral diblocks, the omega-functionalized diblock copolymers constitute a new class of materials which provide the possibility of altering the phase behavior by introducing a small amount of a polar group at one chain end.