AN ANALYTICAL MODEL FOR SOLUTE REDISTRIBUTION DURING SOLIDIFICATION OF PLANAR, COLUMNAR, OR EQUIAXED MORPHOLOGY

Existing models for solute redistribution (microsegregation) during solidification were reviewed. There are no analytical models that take into account limited diffusion in both the liquid and the solid phases. A new analytical mathematical model for solute redistribution was developed. Diffusion in liquid and in solid was considered. This model does not require a prescribed movement of the interface. It can be used for one-dimensional (1-D) (plate), two-dimensional (cylinder), or three-dimensional (3-D) (sphere) calculations. Thus, it is possible to calculate microsegregation at the level of primary or secondary arm spacing for columnar dendrites or for equiaxed dendrites. The solution was compared with calculations based on existing models, as well as with some available experimental data for the segregation of base elements in as cast Al-4.9 wt pct Cu, INCONEL 718, 625, and plain carbon (0.13 wt pct C) steel.