GROWTH OF HIGHLY ORIENTED TIN OXIDE THIN-FILMS BY LASER EVAPORATION DEPOSITION

被引:45
作者
DAI, CM
SU, CS
CHUU, DS
机构
[1] NATL TSING HUA UNIV,INST NUCL SCI,HSINCHU 300,TAIWAN
[2] NATL CHIAO TUNG UNIV,DEPT ELECTROPHYS,HSINCHU,TAIWAN
关键词
D O I
10.1063/1.103998
中图分类号
O59 [应用物理学];
学科分类号
摘要
Conducting and transparent thin films of tin oxide were prepared by the laser evaporation of an undoped powder-pressed polycrystalline tin oxide target onto unheated substrates. After characterizing these films, the results reveal that the films are highly oriented and with a grain size ∼0.2 μm. The nearly stoichiometric deposition of tin oxide films with deposition rates exceeding 24 Å per pulse was obtained by this method. The lowest resistivity obtained is 3.0×10-3 Ω cm. The visible transmittance (between 4000 and 7000 Å) is above 75%.
引用
收藏
页码:1879 / 1881
页数:3
相关论文
共 16 条
[11]   SPRAYED FILMS OF INDIUM TIN OXIDE AND FLUORINE-DOPED TIN OXIDE OF LARGE SURFACE-AREA [J].
POMMIER, R ;
GRIL, C ;
MARUCCHI, J .
THIN SOLID FILMS, 1981, 77 (1-3) :91-97
[12]   EPITAXIAL-GROWTH OF YBA2CU3O7-X THIN-FILMS BY A LASER EVAPORATION PROCESS [J].
ROAS, B ;
SCHULTZ, L ;
ENDRES, G .
APPLIED PHYSICS LETTERS, 1988, 53 (16) :1557-1559
[13]   X-RAY-DIFFRACTION ANALYSIS OF SNO2 FILMS PREPARED BY OXIDATION OF TIN FILMS [J].
SINHA, NP ;
MISRA, M .
THIN SOLID FILMS, 1983, 101 (02) :L33-L34
[14]   TRANSPARENT CONDUCTING SNOX FILMS HIGH-RATE REACTIVELY SPUTTERED ONTO POLYESTER FOIL [J].
STJERNA, B ;
GRANQVIST, CG .
APPLIED OPTICS, 1990, 29 (04) :447-448
[15]   STRUCTURAL, ELECTRICAL AND OPTICAL-PROPERTIES OF RF-MAGNETRON-SPUTTERED SNO2-SB FILM [J].
SUZUKI, K ;
MIZUHASHI, M .
THIN SOLID FILMS, 1982, 97 (02) :119-127
[16]   LOW-TEMPERATURE GROWTH OF TRANSPARENT AND CONDUCTING TIN OXIDE FILM BY PHOTOCHEMICAL VAPOR-DEPOSITION [J].
TABUCHI, T ;
YAMAGISHI, K ;
TARUI, Y .
JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1987, 26 (03) :L186-L189